Comparison of Fe30Co20Cr20Ni20Mo3.5 High Entropy Alloy Coatings Prepared Using Plasma Cladding, High-Speed Laser Cladding, and Deep Laser Cladding

Mengzhao Li,Chao Li,Bingyuan Li,Yicheng Zhou,Long Huang,Ang Cai,Chang Cui,Senao Gao,Guodong Zhang,Bing Yang
DOI: https://doi.org/10.3390/coatings13111819
IF: 3.236
2023-10-24
Coatings
Abstract:Three kinds of Fe30Ni20Co20Cr20Mo3.5 high entropy alloy (HEA) coatings were prepared on the surface of a Q235 steel plate using plasma cladding and laser cladding. The microstructure, crystal structure, element distribution, microhardness, wear resistance, and corrosion resistance of the coatings were studied. The grain size of the high-speed laser cladding coating (HLC) was the smallest. The crystal structures of the plasma cladding coating (PC) and HLC were single face-centered cubic (FCC), while that of the deep laser cladding coating (DLC) was body-centered cubic (BCC). DLC had the best microhardness and wear resistance. The microhardness of PC, HLC, and DLC increased by 70%, 108%, and 109%, respectively, and the average friction coefficient decreased by 33%, 44%, and 51%, respectively, compared to Q235. HLC had the best corrosion resistance, with an annual corrosion rate of 0.66925 mm/a. The annual corrosion rate of PC and HLC was only 40% of Q235. The polarization curves of PC and HLC had obvious passivation regions with a width of up to 2 V. The corrosion types of PC were pitting corrosion and intergranular corrosion, that of HLC was general corrosion, and that of DLC was severe pitting corrosion.
materials science, multidisciplinary,physics, applied, coatings & films
What problem does this paper attempt to address?
The main problems that this paper attempts to solve are to improve the surface hardness, wear resistance and corrosion resistance of Q235 steel. Specifically, the researchers prepared Fe₃₀Co₂₀Cr₂₀Ni₂₀Mo₃.₅ high - entropy alloy (HEA) coatings on the surface of Q235 steel plates by using three different coating techniques (plasma cladding, high - speed laser cladding and deep laser cladding), and compared the microstructure, crystal structure, element distribution, micro - hardness, wear resistance and corrosion resistance of these coatings. ### Summary of main problems: 1. **Improve surface hardness**: The surface hardness of Q235 steel is relatively low and is easily worn. By preparing a high - entropy alloy coating on the surface, its surface hardness can be significantly increased. 2. **Enhance wear resistance**: The wear resistance of Q235 steel is poor, especially when used in harsh environments. By introducing a high - entropy alloy coating, its wear - resistant performance can be improved. 3. **Improve corrosion resistance**: Q235 steel is prone to electrochemical corrosion in humid environments. Through surface modification techniques, especially the application of high - entropy alloy coatings, its corrosion - resistant performance can be effectively improved. ### Research methods: - **Plasma Cladding (PC)**: Use a high - energy plasma beam to melt the powder and deposit it on the surface of the substrate. - **High - Speed Laser Cladding (HLC)**: Use a high - power - density laser beam to quickly melt the powder and form a coating on the substrate. - **Deep Laser Cladding (DLC)**: Use a laser beam with a higher power density to partially melt the substrate and form a metallurgical bond with the melted powder. ### Research objectives: By comparing the properties of Fe₃₀Co₂₀Cr₂₀Ni₂₀Mo₃.₅ high - entropy alloy coatings prepared by three different cladding processes, determine which process can most effectively improve the surface hardness, wear resistance and corrosion resistance of Q235 steel, so as to provide a better choice for industrial applications. ### Key conclusions: - **DLC has the best micro - hardness and wear resistance**, but its corrosion resistance is not as good as that of HLC. - **HLC exhibits the best corrosion resistance**, with an annual corrosion rate of 0.66925 mm/a. - **The micro - hardness of PC, HLC and DLC increased by 70%, 108% and 109% respectively**, and the average friction coefficients decreased by 33%, 44% and 51% respectively. Through this study, the author hopes to provide new ideas and technical support for the surface modification of Q235 steel to meet its application requirements in different industrial fields.