Abstract:Edge located nitrogen (edge-N) species in carbon materials have been commonly recognized as one of the most active sites for Zn2+ storage, by virtue of their more accessible microstructure and lower adsorption energy barrier. However, how to modulate N species types and enrich the concentration of edge-N (pyridinic-N and pyrrolic-N) is still a daunting challenge. In this work, the conversion of graphitic-N to edge-N in carbon matrix was creatively realized by the additional incorporation of boron element and the ratio of edge-N reach up to 81.6% in terms of the total N content. The optimized B-doped rich edge-N porous carbon (BENC) with matchable pore size to accommodate solvated Zn2+ and abundant zincophilic sites exhibits outstanding Zn2+ storage capabilities, which delivers a high reversible capacity (354.6 F g-1 at 0.1 A g-1), excellent power density (126.2 Wh kg-1) and almost no capacity loss after 20000 cycles. Moreover, density functional theory (DFT) calculations further discover that B/edge-N sites reduce the adsorption energy barrier of Zn2+, contributing to the invertible adsorption/desorption of Zn2+. This study demonstrates the synergistic effect of B and N dopants on capacity enhancement in carbon materials for Zn2+ storage applications.

Tuning Nitrogen Species in 3D Porous Carbon via Boron doping for Boosted Zn-ion Storage Capability