Abstract:Composites that use fly ash and slag as alkali-activated materials instead of cement can overcome the defects and negative effects of alkali-activated cementitious materials prepared with the use of an alkali-activated material. In this study, fly ash and slag were used as raw materials to prepare alkali-activated composite cementitious materials. Experimental studies were carried out on the effects of the slag content, activator concentration and curing age on the compressive strength of the composite cementitious materials. The microstructure was characterized using hydration heat, X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), mercury intrusion porosimetry (MIP) and scanning electron microscopy (SEM), and its intrinsic influence mechanism was revealed. The results show that increasing the curing age improves the degree of polymerization reaction and the composite reaches 77~86% of its 7-day compressive strength after 3 days. Except for the composites with 10% and 30% slag content, which reach 33% and 64%, respectively, of their 28-day compressive strength at 7 days, the remaining composites reach more than 95%. This result indicates that the alkali-activated fly ash–slag composite cementitious material has a rapid hydration reaction in the early stage and a slow hydration reaction in the later stage. The amount of slag is the main influencing factor of the compressive strength of alkali-activated cementitious materials. The compressive strength shows a trend of continuous increase when increasing slag content from 10% to 90%, and the maximum compressive strength reaches 80.26 MPa. The increase in the slag content introduces more Ca2+ into the system, which increases the hydration reaction rate, promotes the formation of more hydration products, refines the pore size distribution of the structure, reduces the porosity, and forms a denser microstructure. Therefore, it improves the mechanical properties of the cementitious material. The compressive strength shows a trend of first increasing and then decreasing when the activator concentration increases from 0.20 to 0.40, and the maximum compressive strength is 61.68 MPa (obtained at 0.30). The increase in the activator concentration improves the alkaline environment of the solution, optimizes the level of the hydration reaction, promotes the formation of more hydration products, and makes the microstructure denser. However, an activator concentration that is too large or too small hinders the hydration reaction and affects the strength development of the cementitious material.

An investigation on frost resistance and pore structure of alkali-activated slag concrete

Understanding the Role of Calcium Silicate Slag in Sodium Carbonate-Activated Green Materials: Influence on Kinetics, Strength, and Efflorescence

Freeze-thaw resistance with de-icing salts of alkali-activated slag concrete: the influence of activator type and dosage and comparison to the ordinary Portland cement concrete

Enhancing Freeze-Thaw Resistance of Alkali-Activated Slag by Metakaolin

Chloride transport resistance of alkali-activated concrete exposed to combined chloride, sulfate and carbonation environment

Freeze–thaw resistance and sorptivity of fine‐grained alkali‐activated cement concrete

Hydration Characteristics and Microstructure of Alkali-Activated Slag Concrete: A Review

Microstructure and life prediction model of steel slag concrete under freezing-thawing environment

Changes in Pore Characteristics of Alkali-activated Slag Paste after Freeze-thaw Cycles

Microstructures and properties of alkali-activated slags with composite activator: Effects of Na2O equivalents

Study on Shrinkage in Alkali-Activated Slag–Fly Ash Cementitious Materials

Mechanical Performances and Frost Resistance of Alkali-Activated Coal Gangue Cementitious Materials

Study of the Mechanical Properties and Microstructure of Alkali-Activated Fly Ash–Slag Composite Cementitious Materials

Properties, Microstructure Development and Life Cycle Assessment of Alkali-Activated Materials Containing Steel Slag under Different Alkali Equivalents

Investigation of shrinkage mechanism of alkali-activated slag

Freezing and thawing cycles: effect on recycled aggregate concrete including slag

Experimental Research on Anti-Corrosion of Slag High Performance Concrete

Degradation of alkali-activated slag subjected to water immersion

Study on the Frost Resistance of Composite Limestone Powder Concrete against Coupling Effects of Sulfate Freeze–Thaw

A numerical study on chloride transport in alkali-activated fly ash/slag concretes

Effects of Lithium Slag on the Frost Resistance of Cement-Soil