Enhancement of the electrochemical performance of LiNi0.5Mn1.5O4 cathode materials for Li-ion battery by Mo-F co-doping

Yuling Weng,Hailang Zhang

DOI: https://doi.org/10.1007/s11581-023-05366-4

IF: 2.961

2024-02-08

Ionics

Abstract:The pristine LiNi 0.5 Mn 1.5 O 4 (LNMO) and Mo-F co-doped LiNi 0.5 Mn 1.5 O 4 spinel materials were prepared via a rheological phase method. The four samples were analyzed by X-ray diffraction (XRD), Fourier transform infrared spectrometer (FTIR), scanning electron microscopy (SEM), energy dispersive spectrometer (EDS), transmission electron microscope (TEM), and X-ray photoelectron spectroscopy (XPS). Compared with the pristine LNMO sample, Mo-F co-doped LNMO materials could increase the lattice parameters, reduce particle sizes, and significantly improve the electrochemical performances of LNMO. The doped material exhibited optimum electrochemical properties when the Mo and F doping amounts were 1% and 3%, respectively, denoted as Mo/F-2. The discharge capacity retention of Mo/F-2 is 95.6%, which is higher than the pristine sample (87.7%) after 100 cycles at 1C and room temperature. Furthermore, the discharge-specific capacity of the Mo/F-2 sample reaches 113.4 mAh g −1 at 5C, while the pristine sample reaches only 61.9 mAh g −1 . After CV and EIS analysis, it was found that the Mo-F co-doped LNMO materials had better Li + diffusion kinetics than the pristine LNMO sample. Thus, Mo-F co-doping is considered an effective modification method for LNMO cathode material.

chemistry, physical,physics, condensed matter,electrochemistry