Abstract:YAG: 5 mol%Yb3+/x mol%Nd3+(x = 0, 0.5, 1, 2, 4, 7) and YAG: 2 mol%Nd3+ single crystal (SC) fluorescent materials were prepared using laser heated pedestal growth (LHPG) method. The up-conversion (UC) spectra of YAG: Yb3+/Nd3+ were recorded under 980 nm laser excitation, the results show that the optimal material was obtained at 5 mol%Yb3+/2 mol%Nd3+. An integrated YAG single crystal fiber (SCF) with end 5 mol%Yb3+/2 mol %Nd3+ co-doped was prepared by the LHPG method, the temperature-dependent characteristics were measured in the range from 348 K to 1448 K. It shows that the fluorescence intensity increases and then decreases with the increase of temperature. Fluorescence intensity ratios (FIR) in Nd3+ UC spectra, including FIR1 (4F7/2/4F5/2 -> 4I9/2), FIR2 (4F9/2/4F5/2 -> 4I9/2) and FIR3 (4G5/2/4F9/2 -> 4I9/2), vary monotonically in temperature ranges of 348-1273 K, 523-1273 K, and 673-1273 K, respectively. The maximally absolute and relative sensitivities for FIR1 were, respectively, achieved to be 2.34 x 10-3 K-1 at 738 K and 4.61 x 10-1 %K-1 at 390 K, and these values for FIR2 were accordingly achieved to be 1.19 x 10-3 K-1 at 1273 K and 4.59 x 10-1 %K-1 at 735 K, and for FIR3 they were 4.66 x 10-3 K-1 at 1273 K and 4.09 x 10-1 %K-1 at 760 K. Therefore, we believe that the fabricated YAG: Yb3+/Nd3+ fluorescent materials have favorable application potential for optical thermometer.

Thermo-optic characterization of Yb:CaGdAlO 4 laser crystal

Disordered Yb:GdYCOB Crystal: Polarized Spectroscopy, Thermal Lensing and Diode-Pumped Lasers

Thermal conductivity versus Yb3+ concentration in Yb:CALGO: A material for high power ultrafast laser

Spectroscopic, Thermal, and Laser Properties of Yb:CaNb $_{2}$ O $_{6}$ Crystal

Study of Pure and Yb~(3+)-doped GdAl_3(BO_3)_4 Crystal

Growth of Yb-doped Ca4GdO(BO3)3 Crystals and Their Spectra and Laser Properties

Spectroscopic Properties of Yb3+‐doped Ca4Gd0.5Y0.5O(BO3)3 Single Crystals

Dual-wavelength and Efficient Continuous-Wave Operation of a Yb:CaGd0.1Y0.9AlO4laser

Laser oscillation with low quantum defect in Yb:GdVO4, a crystal with high thermal conductivity.

Growth, spectroscopy and SESAM mode-locking of a "mixed" Yb:Ca(Gd,Y)AlO4 disordered crystal

Anisotropy of thermal and spectral characteristics in Tm:YAP laser crystals

Optical Temperature Sensing Characteristics of Yb3+/Nd3+ Co-Doped YAG Single Crystal Fiber Based on Up-Conversion Luminescence

Laser emission with low quantum defect in Yb: CaGdAlO4.

Growth and Noncritical Phase-Matching Third-Harmonic-generation of GdxY1−xCa4O(BO3)3 Crystal

Spectral properties and high-efficiency broadband laser operation of Tm:CaY0.9Gd0.1AlO4 crystal

Optical temperature sensitivity, up-conversion luminescence and structure of Ca5 (PO4)3F: Yb3+, Ho3+, Tm3+ glass-ceramics

Sensitivity-enhanced Tm 3+ /yb 3+ Co-Doped YAG Single Crystal Optical Fiber Thermometry Based on Upconversion Emissions

Remarkable temperature-dependent second-harmonic-generation performance of a YCOB crystal

Continuous-wave and Passively Mode-Locked Operation of Yb:Ca3Gd2(BO3)4 Laser

Spectroscopic Characteristics and Laser Performance of Tm:Cayalo4 Crystal

Crystal growth, spectra properties, and 2-μm laser performance of a novel “mixed” Tm3+-doped CaY0.65Gd0.35AlO4 crystal