Abstract:Zinc oxide, as a widely used material in optics, electronics, and medicine, requires a complete overview of different conditions for facile and easily reproducible syntheses. Two types of optimization of ZnO hydrothermal preparation from zinc acetate and sodium hydroxide solution are presented, which allowed for obtaining miscellaneous morphologies of materials. The first was a temperature-controlled synthesis from 100 to 200 °C, using citric acid as a capping agent. The formation of hexagonal rods at the lowest temperature was evidenced, which agglomerated to flower-like structures at 110 and 120 °C. It was followed by transformation to flake-like roses at 160 °C, up to disordered structures composed of nanosized plates (>180 °C). The transformations were generated through a temperature change, which had an impact on the diffusion effect of hydroxide and citrate complexes. The second optimization was the hydrothermal synthesis free of organic additives and it included only a pH variation from 7.5 to 13.5. It was found that by utilizing a slow-dropping process and varying amounts of NaOH solutions, it is possible to obtain well-formed hexagonal pellets at pH 8.0-8.5. Strongly basic conditions of pH 11.0 and 13.5 impeded superstructure formations, giving small elongated particles of ZnO. All samples were characterized by high phase purity and crystallinity, with a specific surface area of 18-37 m2/g, whereas particle size distribution indicated a predominance of small particles (<1 μm).

Influence of hydrothermal conditions on the morphology and particle size of zinc oxide powder

Morphology Investigation of Hydrothermally Prepared ZnO Micro-Crystals Influenced by Cu2+ Ions

Influence of Microwave Hydrothermal Conditions on the Morphology and Particle Size of Zinc Oxide Crystailite

Hydrothermal synthesis of zinc oxide powders with different morphologies

Hydrothermal synthesis of zinc oxide powders with controllable morphology

Effect of Reaction Temperature on Surface Morphology and Photoelectric Properties of ZnO Grown by Hydrothermal Method in Mixed Solvent

Synthesis of Single-Crystalline Pb(Zr0.52Ti0.48)O-3 Nanocrystals by Hydrothermal Method

Hydrothermal Synthesis of ZnO Superstructures with Controlled Morphology via Temperature and pH Optimization

Hydrothermal synthesis and characterization of Zinc Oxide nanoparticles of various shapes under different reaction conditions

The mechanism for hydrothermal growth of zinc oxide

Sequential Occurrence of ZnO Nanopaticles, Nanorods, and Nanotips During Hydrothermal Process in a Dilute Aqueous Solution

Hydrothermal Preparation of CuAlO2 Powder

Supercritical hydrothermal synthesis of nano-ZnO: Effects of key parameters and reaction mechanism

Effect of alkali metal hydroxide on formation processes of zinc oxide crystallites from aqueous solutions containing Zn(OH)42? ions

Study on the Synthesis of Nano Zinc Oxide Particles under Supercritical Hydrothermal Conditions

Recent Progress in Hydrothermal Synthesis of Zinc Oxide Nanomaterials

A Simple and Novel Low-Temperature Hydrothermal Synthesis of ZnO Nanorods

Hydrothermal synthesis of one-dimensional zinc oxides with different precursors

Hydrothermal Synthesis of Lead Zirconate Titanate Nearly Free-Standing Nanoparticles in the Size Regime of about 4 Nm

Effects of KOH and Temperature on Hydrothermal Synthesis of Α-Feooh Nanowire