Abstract:To reduce the losses caused by the atmospheric corrosion of carbon steels, it is important to establish a prediction model to determine the corrosion rate of carbon steels in natural environments. In this study, a prediction model of atmospheric corrosion of Q235 carbon steel (PMACC-Q235) in China was established by coupling the mean impact value algorithm and back propagation artificial neural network. Tempo-spatial patterns of corrosion rates in five long-exposure time categories across China were analyzed. Ten main factors affecting the atmospheric corrosion of Q235 were identified. The corrosion rates in a single year were similar (approximately 30 μm/a) and larger than those for 2 (25.30 μm/a) and 3 years (21.66 μm/a). The spatial corrosion rates in the northwestern areas were primarily lower than those in southeastern coastal areas. This could be influenced by climatic factors, such as temperature, humidity, and precipitation. All corrosion rates reached the C2 level (>1.3 μm/a), and there was some possibility that they reached higher corrosion levels. The largest probability for the C3 level in all periods was an average of 0.91, and that for the C4 level was 0.83. Spatially, higher probabilities were mainly located in the southern area, especially in Hainan, located in the south and surrounded by sea. Corrosion rates largely varied among climatic zones, and mean corrosion rates in the tropical monsoon climate zone were the largest (average of three periods 33.39 μm/a). SO2 and soluble-dust fall had the largest impact on the variations in the corrosion rates among different climatic zones.

Atmospheric corrosion of AISI‐1020 carbon steel in a very aggressive coastal zone of Havana, Cuba. Determination of corrosivity category using three ways of assessment

Atmospheric corrosion of carbon steel: Results of one-year exposure in an andean tropical atmosphere in Colombia

Corrosion of Carbon Steel in a Tropical Marine Environment Enhanced by H2S from Sargassum Seaweed Decomposition

Atmospheric chloride-induced corrosion of steel-reinforced concrete beam exposed to real marine-environment for 7 years

Characterization of Corrosion Products Formed on Q235 Carbon Steel and T2 Copper in the Antarctic Atmosphere

Considerations for realistic atmospheric environments: An application to corrosion testing

Corrosion Behavior of Q235 Steel in Atmospheres Containing SO2 and NaCl

Investigation of Microstructure and Corrosion Behavior of Weathering Steel in Aqueous Solution Containing Different Anions for Simulating Service Environments

Chloride-induced Corrosion Patterns of Reinforcements in Simulated Pore Solutions of Calcium Sulfoaluminate Cement Concrete: an Analytical Study

Investigation on the initial atmospheric corrosion of mild steel in a simulated environment of industrial coastland by thin electrical resistance and electrochemical sensors

Atmospheric Corrosion of Steel A3 Deposited with Ammonium Sulfate and in the Presence of Sulfur Dioxide

Influence of Stochastic Chlorine Environment on the Spatiotemporal Deterioration of Marine RC Structures

Atmospheric Corrosion Behaviour of Pure Al 1060 in Tropical Marine Environment

Chloride penetration in concrete under marine atmospheric environment – analysis of the influencing factors

Corrosion of steel materials in four environmental conditions

Influence of SO<sub>2</sub> Concentration on Initial Corrosion of Aluminum in Marine Atmosphere

Corrosion-Mechanical Properties and Susceptibility to Hydrogenetaion of Pipe Steel in the Presence of Carbon Dioxide Gas and Hydrogen Sulphide in Environment

Numerical Approach for Atmospheric Corrosion Monitoring Based on EIS of a Weathering Steel

The effect of variable humidity on corrosion fatigue of AA7085-T7451 with surface salt deposits

Prediction of Tempo-Spatial Patterns and Exceedance Probabilities of Atmospheric Corrosion of Q235 Carbon Steel Across China

Initial Corrosion of Steel in Cement-Based Composites in Saline Soil at 65°C