Preparation of Ni3S2 Electrocatalyst from Different Sulfur Sources and its Performance in Electrocatalytic Hydrogen Evolution Reaction

DOI: https://doi.org/10.1007/s10562-024-04737-4

IF: 2.936

2024-06-09

Catalysis Letters

Abstract:A series of Ni 3 S 2 electrocatalysts were successfully prepared using nickel foam precursor as substrate and thiourea, sodium thiosulfate pentahydrate, sodium sulfide nonahydrate and sodium diethyldithiocarbamate as sulfur sources, and their performances in electrocatalytic hydrogen evolution (HER) were further compared. The results exhibited that the Ni 3 S 2 catalyst prepared with sodium thiosulfate pentahydrate as the sulfur source showed the best performance in HER. At a current density of 10 mA cm −2 , the overpotential was only 178 mV, and the Tafel slope was 70.4 mV dec −1 . In addition, through the double-layer capacitance test, it was found that the catalyst had the highest electrochemical active area, and the capacitance reached 41.33 mF cm −2 , which was consistent with its excellent HER performance. In this work, the influence mechanism of different sulfur sources on the sulfurization process of Ni 3 S 2 catalyst and the further impact of these effects on the performance of HER were also discussed in detail. These results provide a solid theoretical and experimental basis for optimizing the application of Ni 3 S 2 catalyst in the field of electrocatalytic hydrogen production.

chemistry, physical