Abstract:A novel co-roasting of red mud and coal gangue is presented.Fe and Al minerals could be effectively separated and enriched by co-roasting.Concentrate of the iron content of 57.25% and recovery of 65.22% is obtained.Fe content in magnetite is raised to 67.30% in product from 0.26% in raw material.Resource utilization of red mud and coal gangue is realized.Red mud and coal gangue are industrial solid wastes discharged during alumina extraction and coal mining, respectively. As these are hazardous materials, their disposal leads to serious environmental issues. In this study, an innovative utilization of red mud through co-roasting with coal gangue for separation and recycling of iron and aluminum minerals is presented. Under optimum co-roasting conditions (550 °C for 50 min), an iron concentrate containing 57.25% TFe (total iron content) with the recovery of 65.22%, and an aluminum-rich product containing 27.26% Al2O3 with the recovery of 71.37% were obtained after magnetic separation. The characteristics of mixed raw material and products all indicated that the goethite and hematite phases in the mixed raw material were transformed into a magnetite phase after co-roasting, although some of the magnetite generated during co-roasting was oxidized to hematite again. This study demonstrates that co-roasting of coal gangue and red mud is a promising technology for the reduction of iron and activation of aluminum to realize resource recycling without additional materials.<ol class="links-for-figure"><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S1226086X21001611-fx1_lrg.jpg">Download : Download high-res image (143KB)</a></li><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S1226086X21001611-fx1.jpg">Download : Download full-size image</a></li></ol>

Innovative utilization of red mud through co-roasting with coal gangue for separation of iron and aluminum minerals

Recovery of iron from high-iron red mud using suspension magnetization roasting and magnetic separation

Extraction of Iron and Alumina from Red Mud with a Non-Harmful Magnetization Sintering Process

Clean utilization of high-iron red mud by suspension magnetization roasting

Reductive roasting of red mud with carbon and sulfuric acid dissolution of iron and aluminum: Transformation phases and leaching characteristics

Extraction of Fe and Al from red mud using carbothermic reduction followed by water leaching

Stepwise extraction of valuable components from red mud based on reductive roasting with sodium salts

Iron Extraction from Red Mud using Roasting with Sodium Salt

Iron Recovery from Red Mud Using Carbothermic Roasting with Addition of Alkaline Salts

Study on Extraction Valuable Metal Elements by Co-Roasting Coal Gangue with Coal Gasification Coarse Slag

Study on Magnetization Roasting Kinetics of High-Iron and Low-Silicon Red Mud

Green and Efficient Utilization of Ferruginous Gibbsite Ore and Ferruginous Manganese Ore by Synergetic Carbothermic Co-Reduction–Magnetic Separation Process

Comprehensive Utilization of Al-Goethite-Containing Red Mud Treated Through Low-Temperature Sodium Salt-Assisted Roasting–Water Leaching

High‐efficiency Preparation of Fe–Al Based Flocculants from Red Mud by Microwave Selective Carbothermic Reduction and Magnetic Separation

An efficient and clean utilization technique for red mud based on fluidized bed carbon monoxide reduction

Co-pyrolysis of biomass with Red Mud: An efficient approach to improving bio-oil quality and resourceful utilization of the iron in Red Mud

A New Strategy for Collaborative Utilization of Red Mud and Coal Fly Ash via Vacuum Reduction Technology

Application of Bayer red mud for iron recovery and building material production from alumosilicate residues

Optimizing iron separation and recycling from iron tailings: A synergistic approach combining reduction roasting and alkaline leaching

Extraction of valuable critical metals from coal gangue by roasting activation-sulfuric acid leaching

Efficient utilization of red mud waste via stepwise leaching to obtain α-hematite and mesoporous γ-alumina