Viscoelastic Behavior and Phase Structure of High-Content SBS-Modified Asphalt

Dongdong Yuan,Chengwei Xing,Wei Jiang,Jingjing Xiao,Wangjie Wu,Pengfei Li,Yupeng Li

DOI: https://doi.org/10.3390/polym14122476

IF: 5

2022-06-18

Polymers

Abstract:To investigate the effect of styrene-butadiene-styrene (SBS) modifier content on the viscoelastic behavior of SBS-modified asphalt (SBSMA) at different temperatures and phase structures, the star SBS modifier was chosen to fabricate seven types of SBSMA with different contents. Multiple stress creep recovery (MSCR), linear amplitude sweep (LAS), and low-temperature frequency sweep tests were adopted to study the influence of SBS modifier content on the viscoelastic performance of SBSMA at high to low temperatures. The SBSMA's microstructure with different contents was investigated using a fluorescence microscope. The results indicated that the change in non-recoverable creep compliance and creep recovery rate was bounded by 4.5% content at high temperatures, with an apparent turning point. The changing slope of content at less than 4.5% was much higher than that of the content greater than 4.5%. At medium temperatures, the fatigue life of SBSMA increased exponentially with the rising modifier content. The rate of increase in fatigue life was the largest as the content increased from 4.5% to 6.0%. At low temperatures, the low-temperature viscoelastic property index G (60 s) of SBSMA decreased logarithmically as the modifier content increased. In terms of the microscopic phase structure, the SBS modifier gradually changed from the dispersed to the continuous phase state with the increasing SBS modifier content.

polymer science

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to explore the viscoelastic behavior and phase structure of high - content SBS - modified asphalt (SBSMA) at different temperatures. Specifically, the research purposes are:

1. **Evaluate the influence of SBS modifier content on the viscoelastic properties of SBSMA**: Through multiple stress creep recovery (MSCR), linear amplitude scan (LAS) and low - temperature frequency scan tests, study the influence of SBS modifier content on the viscoelastic properties of SBSMA at high, medium and low temperatures.

2. **Analyze the micro - phase structure of SBSMA**: Use fluorescence microscopy to analyze the micro - phase structure of SBSMA with different contents of SBS modifier, in order to understand the relationship between its phase state change and macroscopic properties.

3. **Provide references for the application of high - content SBS - modified asphalt**: Through the above - mentioned experiments and analyses, provide scientific basis and technical support for the wider application of high - content SBS - modified asphalt.

### Research background

With the increase of traffic loads, ordinary asphalt binders can no longer meet the requirements of modern traffic development. Styrene - butadiene - styrene (SBS) - modified asphalt is widely used in highway construction because of its excellent durability, anti - aging, anti - fatigue and anti - water - damage properties. However, at present, there are relatively few studies on high - content SBS - modified asphalt, especially the lack of detailed discussions on its viscoelastic behavior and phase structure. Therefore, this study aims to fill this gap and provide theoretical support for the application of high - content SBS - modified asphalt.

### Main methods

In order to achieve the above - mentioned goals, the researchers adopted the following methods:

- **Material preparation**: Seven SBS - modified asphalt samples with different contents (3.0%, 4.5%, 6.0%, 7.5%, 9.0%, 10.5% and 12.0%) were selected and tested using a dynamic shear rheometer (DSR).

- **Testing methods**:
- **MSCR test**: Used to evaluate the viscoelastic behavior of SBSMA at high temperatures.
- **LAS test**: Used to evaluate the fatigue performance of SBSMA at medium temperatures.
- **Low - temperature frequency scan test**: Used to evaluate the viscoelastic behavior of SBSMA at low temperatures.

- **Micro - structure analysis**: Use fluorescence microscopy to observe the micro - phase structure of SBSMA with different contents of SBS modifier.

### Key findings

The research results show that:

- At high temperatures, the change of SBS modifier content has a significant influence on the non - recovered creep compliance (\( J_{nr} \)) and the creep recovery rate (\( R \)), and there is an obvious turning point (4.5%). After exceeding this turning point, the improvement effect is limited.
- At medium temperatures, the increase of SBS modifier content significantly improves the fatigue life of SBSMA, especially in the range of 4.5% - 6.0%, where the increase in fatigue life is the most obvious.
- At low temperatures, the increase of SBS modifier content leads to a logarithmic decrease in the low - temperature viscoelastic performance index \( G(60\,s) \) of SBSMA.
- Micro - phase structure analysis shows that with the increase of SBS modifier content, SBS gradually changes from the dispersed phase to the continuous phase.

These findings provide important theoretical basis and technical guidance for the application of high - content SBS - modified asphalt in actual engineering.