2D/3D heterojunction engineering at the buried interface towards high-performance inverted methylammonium-free perovskite solar cells

Haiyun Li,Cong Zhang,Cheng Gong,Daliang Zhang,Hong Zhang,Qixin Zhuang,Xuemeng Yu,Shaokuan Gong,Xihan Chen,Jiabao Yang,Xuanhua Li,Ru Li,Jingwei Li,Jinfei Zhou,Hua Yang,Qianqian Lin,Junhao Chu,Michael Grätzel,Jiangzhao Chen,Zhigang Zang

DOI: https://doi.org/10.1038/s41560-023-01295-8

IF: 56.7

2023-07-07

Nature Energy

Abstract:The main bottlenecks limiting the photovoltaic performance and stability of inverted perovskite solar cells (PSCs) are trap-assisted non-radiative recombination losses and photochemical degradation at the interface between perovskite and charge-transport layers. We propose a strategy to manipulate the crystallization of methylammonium-free perovskite by incorporating a small amount of 2-aminoindan hydrochloride into the precursor inks. This additive also modulates carrier recombination and extraction dynamics at the buried interface via the formation of a bottom-up two-dimensional/three-dimensional heterojunction. The resultant inverted PSC achieves a power conversion efficiency of 25.12% (certified 24.6%) at laboratory scale (0.09 cm 2 ) and 22.48% at a larger area (1 cm 2 ) with negligible hysteresis. More importantly, the resulting unencapsulated devices show superior operational stability, maintaining >98% of their initial efficiency of >24% after 1,500 hours of continuous maximum power point tracking under simulated AM1.5 illumination. Meanwhile, the encapsulated devices retain >92% of initial performance for 1,200 hours under the damp-heat test (85 °C and 85% relative humidity).

materials science, multidisciplinary,energy & fuels