Microwave assisted synthesis of ErxYbyCa1-x-yMoO4 nano-phosphor for efficient temperature sensing and catalytic applications

Sourabh Gouraha,Neha Jain,Kumari Anchal,Geetika Patel,Subhash Banerjee,Jai Singh

DOI: https://doi.org/10.1038/s41598-024-71478-0

IF: 4.6

2024-11-10

Scientific Reports

Abstract:Here, Er/Yb Co-doped CaMoO 4 materials (Er x Yb y Ca 1−x−y MoO 4 NPs where x = 0, 0.01 and y = 0, 0.05, 0.10, 0.15, 0.20) were prepared by microwave-assisted method and its pure-tetragonal structure were confirmed by X-ray diffraction spectra (XRD), Rietveld-refinement and Raman-vibrational spectra. The transmission-electron microscopy (TEM) study indicates the formation of nearly spherical shaped nanomaterial with average size of ~ 15 nm. Additionally, absorption and emission properties were studied by UV–Visible–NIR and photoluminescence (PL) spectrometer. The UV–Visible–NIR spectra attribute absorption of Er 3+ ion in visible region (380–700 nm) and absorption of Yb 3+ ion in near-infrared region (700–1400 nm). Moreover, PL up-conversion spectra of the sample recorded under excitation wavelength 980 nm. The PL peaks were observed at 530, 544–552, and 656–670 nm. Prominent PL-intensity was observed for Er 0.01 Yb 0.15 Ca 0.84 MoO 4 phosphor. Temperature dependent PL study reveals that present phosphor is robust phosphor for temperature sensor. In addition, Er 3+ /Yb 3+ doped CaMoO 4 nanomaterials exhibited excellent activity and selectivity in the aerial oxidation of benzoin over benzyl under oxidant-free reaction conditions. The synergistic effect Er 3+ /Yb 3+ co-doing in CaMoO 4 matrix was observed, where only CaMoO 4 material found to be inactive towards above oxidation reaction. Moreover, the oxidation of primary benzyl-alcohols was furnished in presence of tertiary butyl hydroperoxideas oxidant.

multidisciplinary sciences