Synergistic Catalytic Mechanism between Ni and Carbon Aerogel for Dehydrogenation of Mg-Based Hydrides

Rui Shi,Jiguang Zhang,Yunfeng Zhu,Yana Liu,Xiaohui Hu,Yao Zhang,Wei Su,Liquan Li

DOI: https://doi.org/10.1021/acs.energyfuels.0c02218

2020-07-24

Abstract:Adding hybrid catalyst is an effective method to improve the hydrogen desorption properties of the Mg-based materials. In this paper, the synergistic catalytic mechanism between Ni and carbon aerogel (CA) was investigated in detail, experimentally and theoretically. The hybrid catalyst of Ni-doped CA (Ni/CA) showed better catalytic performance than pure Ni or CA: the dehydrogenation activation energy of the Mg–Ni composite hydrides was drastically reduced to 86.3 kJ/mol after the introduction of Ni/CA. This synergistic catalytic effect between Ni and CA was attributed to the charge transfer between Ni, CA, and MgH₂ according to density functional theory calculations. Such a charge transfer could raise the d-band center of the surface nickel atoms from −1.468 to −1.399 and −1.434 eV, leading to a stronger H affinity of Ni after hybridization with CA. MgH₂ can be further destabilized because the carbon atoms could act as electron acceptors to seize the electrons from the Mg–H bond and, thus, lead to a weakened Mg–H bond strength. This synergistic catalytic mechanism may provide novel ideas to design efficient catalysts in hydrogen storage and other related fields.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.energyfuels.0c02218?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.energyfuels.0c02218</a>.Rietveld analysis results of the as-synthesized Mg₉₅Ni₅ (Figure S1), XRD patterns of (a) MM-Mg95Ni5, (b) MM-Mg₉₅Ni₅-CA, (c) MM-Mg₉₅Ni₅-Ni, and (d) MM-Mg₉₅Ni₅-Ni/CA (Figure S2), isothermal dehydrogenation curves of MM-Mg₉₅Ni₅ and MM-Mg₉₅Ni₅-X (X = Ni, CA, and Ni/CA) at 250 °C with an initial hydrogen pressure of 0.005 MPa (Figure S3), SEM images of (a) MM-Mg₉₅Ni₅, (b) MM-Mg₉₅Ni₅-CA, (c) MM-Mg₉₅Ni₅-Ni, and (d) MM-Mg₉₅Ni₅-Ni/CA (Figure S4), (a) side view of the close-packed (3 × 3) Ni(111) slab model and (b and c) top view (only the first layer) of the pure Ni slab model and impurity model with Ni atoms in gray and carbon atoms in brown (Figure S5), schematic diagram of the first atomic layer of the impurity model (Figure S6), and three-dimensional charge density difference plots for the MgH₂ molecule (Mg atoms in orange and H atoms in pink) catalyzed by (a) pure Ni and (b) hybrid catalyst of Ni/CA (nickel atoms in gray and carbon atoms in brown) (Figure S7) (<a class="ext-link" href="/doi/suppl/10.1021/acs.energyfuels.0c02218/suppl_file/ef0c02218_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

energy & fuels,engineering, chemical