Abstract:Electrospun hybrid scaffolds composed of synthetic and natural polymers have gained increasing interest in tissue engineering applications over the last decade. In this work, scaffolds composed of polylactic acid electrospun fibers, either treated (P-PLA) or non-treated (PLA) with air-plasma, were coated with high molecular weight chitosan to create a core–shell microfibrous structure. The effective thickness control of the chitosan layer was confirmed by gravimetric, spectroscopic (FTIR-ATR) and morphological (SEM) investigations. The chitosan coating increased the fiber diameter of the microfibrous scaffolds while the tensile mechanical tests, conducted in dry and wet environments, showed a reinforcing action of the coating layer on the scaffolds, in particular when deposited on P-PLA samples. The stability of the Chi coating on both PLA and P-PLA substrates was confirmed by gravimetric analysis, while their mineralization capacity was evaluated though scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS) after immersing the scaffolds in simulated body fluids (SBF) at 37 °C for 1 week. Sample biocompatibility was investigated through cell viability assay and SEM analysis on mouse pre-osteoblastic MC3T3-E1 cells grown on scaffolds at different times (1, 7, 14 and 21 days). Finally, Alizarin Red assay and qPCR analysis suggested that the combination of plasma treatment and chitosan coating on PLA electrospun scaffolds influences the osteoblastic differentiation of MC3T3-E1 cells, thus demonstrating the great potential of P-PLA/chitosan hybrid scaffolds for bone tissue engineering applications.

What problem does this paper attempt to address?

### Problems the paper attempts to solve This paper aims to promote the osteogenic differentiation of mouse pre - osteoblast MC3T3 - E1 by improving the electrospun core - shell structure scaffolds of polylactic acid (PLA) and chitosan (Chi), thereby enhancing the application potential of these scaffolds in bone defect repair. Specifically, the research focuses on the following aspects: 1. **Improving the surface properties of the scaffolds**: Improve the hydrophilicity and cell compatibility of PLA electrospun fibers through air plasma treatment (P - PLA) and chitosan coating. 2. **Enhancing mechanical properties**: Evaluate the influence of chitosan coating on the mechanical properties of PLA fibers, especially in dry and wet environments. 3. **Promoting mineralization ability**: Analyze by scanning electron microscope (SEM) and energy - dispersive spectroscopy (EDS) to evaluate the mineralization ability of the scaffolds after immersion in simulated body fluid (SBF). 4. **Promoting cell proliferation and differentiation**: Evaluate the effects of differently treated scaffolds on the proliferation, differentiation and gene expression of MC3T3 - E1 cells through cell viability assay, SEM analysis, Alizarin Red staining and qPCR analysis. ### Main research methods - **Material preparation**: Prepare PLA fibers by electrospinning technology and perform air plasma treatment (P - PLA) on them. Subsequently, coat PLA and P - PLA fibers with chitosan solutions of different concentrations to form a core - shell structure. - **Characterization methods**: Characterize the surface properties, morphology, mechanical properties and hydrophilicity of the scaffolds by using X - ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FTIR - ATR), scanning electron microscope (SEM), energy - dispersive spectroscopy (EDS), contact angle measurement, etc. - **Biological evaluation**: Evaluate the effects of differently treated scaffolds on MC3T3 - E1 cells through cell viability assay, SEM analysis, Alizarin Red staining and qPCR analysis. ### Key findings - **Surface properties**: Plasma treatment and chitosan coating significantly improve the hydrophilicity and cell compatibility of PLA fibers. - **Mechanical properties**: Chitosan coating enhances the mechanical properties of PLA fibers, especially in a wet environment. - **Mineralization ability**: The scaffolds with chitosan coating show better mineralization ability in SBF. - **Cell behavior**: The scaffolds with plasma treatment and chitosan coating promote the proliferation and osteogenic differentiation of MC3T3 - E1 cells, manifested as higher cell viability, more calcium deposition and up - regulation of related gene expression. ### Conclusion This research shows that through plasma treatment and chitosan coating, the surface properties, mechanical properties and biocompatibility of PLA electrospun fiber scaffolds can be significantly improved, thus having potential application value in bone tissue engineering.

Improvement of Osteogenic Differentiation of Mouse Pre-Osteoblastic MC3T3-E1 Cells on Core–Shell Polylactic Acid/Chitosan Electrospun Scaffolds for Bone Defect Repair

Promotion of In Vitro Osteogenic Activity by Melt Extrusion-Based PLLA/PCL/PHBV Scaffolds Enriched with Nano-Hydroxyapatite and Strontium Substituted Nano-Hydroxyapatite

PLLA Membranes Enriched with Chitosan/DCPA: Innovative Approach to Bone Tissue Engineering

In Vitro Biocompatibility Assessment of Bioengineered PLA-Hydrogel Core-Shell Scaffolds with Mesenchymal Stromal Cells for Bone Regeneration

Hybrid Core-Shell Polymer Scaffold for Bone Tissue Regeneration

Innovative electrospun PCL/fibroin/l-dopa scaffolds scaffolds supporting bone tissue regeneration

Electrospun scaffolds based on a PCL/starch blend reinforced with CaO nanoparticles for bone tissue engineering

Multilayer Electrospun Scaffolds of Opposite-Charged Chitosans

Enhanced bioactivity of osteoblast-like cells on poly(lactic acid)/poly(methyl methacrylate)/nano-hydroxyapatite scaffolds for bone tissue engineering

Characterization on Modification and Biocompatibility of PCL Scaffold Prepared with Near-field Direct-writing Melt Electrospinning

Poly(L-co-D,L lactic acid-co-Trimethylene Carbonate) 3D printed scaffold cultivated with mesenchymal stem cells directed to bone reconstruction: In vitro and in vivo studies

Bioactivity assessment of PLLA/PCL/HAP electrospun nanofibrous scaffolds for bone tissue engineering

Electrospun PCL/PLA/HA Based Nanofibers as Scaffold for Osteoblast-Like Cells

3D- Printed Poly(ε-caprolactone) Scaffold Integrated with Cell-laden Chitosan Hydrogels for Bone Tissue Engineering

Formulation and Characterization of Chitosan-Based Mixed-Matrix Scaffold for Tissue Engineering

Effects of ceramic additives and bioactive coatings on the degradation of polylactic acid‐based bone scaffolds under hydrolytic conditions

An improved surface for enhanced stem cell proliferation and osteogenic differentiation using electrospun composite PLLA/P123 scaffold

Alendronate crosslinked chitosan/polycaprolactone scaffold for bone defects repairing

Hyaluronic Acid and a Short Peptide Improve the Performance of a PCL Electrospun Fibrous Scaffold Designed for Bone Tissue Engineering Applications

Electrospun PCLJPLAIHA based nanofibers as scaffold for osteoblast-like cells

Microporous polylactic acid/chitin nanocrystals composite scaffolds using in-situ foaming 3D printing for bone tissue engineering