Zincophilic MOF with N-functional groups for interfacial modification of stable aqueous zinc metal anodes

Na Sun,Han Yu,Xue Zhou,Xiuwen Si,Peng-Fei Wang,Zhe Gong,Yaguang Sun,Ming-Dong Zhou

DOI: https://doi.org/10.1039/d4tc02883j

IF: 6.4

2024-11-06

Journal of Materials Chemistry C

Abstract:Rechargeable aqueous batteries using zinc as anode have attracted more and more attention. However, the uncontrolled dendrite growth and hydrogen evolution reaction seriously hinder the performance of zinc anode. In this work, a two-dimensional (2D) zinc-based MOF (ZHPCA) was synthesized by a simple solvothermal method, which is a Zn (II) coordination polymer with mixed ligands of nitrogen and oxygen donors (H-PCA). Using this MOF as the interface modification layer of the Zn electrode, ZHPCA@UZn anode was prepared. The N-functional groups in ZHPCA can be used as binding sites for zinc ion deposition and promote their uniform deposition on zinc anode. The modified layer also effectively inhibited hydrogen evolution and corrosion. The ZHPCA@UZn||ZHPCA@UZn symmetric cells showed a stable cycle of 650 h at a ampere density of 3 mA cm-2. The zinc ion capacitor assembled by matching ZHPCA@UZn anode with activated carbon cathode maintained the specific capacity of 85 mAh g-1 after 1000 cycles at 1 A g-1. To sum up, ZHPCA, the MOF selected in this work, can effectively protect the zinc anode, which has certain inspiration for the selection of zinc anode coating materials in the future.

materials science, multidisciplinary,physics, applied