Copper Slag as an Alternative to Silica Sand for A356 Alloy Casting-Feasibility Study

Dheerendra Singh Patel,Ramesh Kumar Nayak

DOI: https://doi.org/10.1007/s40962-024-01442-1

2024-09-26

International Journal of Metalcasting

Abstract:Silica sand is the most commonly used aggregate in the green sand molding process. This study examines the feasibility of copper slag (Cu slag) as a substitute for commercial-grade silica sand in the green sand mold casting process. The major composition of Cu slag is silica, ferric oxide, and alumina. The central composite design within the framework of response surface methodology (RSM) is a quintessential method and used for the optimization of mold constituents of Cu slag molds. The RSM model predicted 3.1 wt% moisture and 11.2 wt% bentonite clay in the Cu slag mold to achieve the required mold properties. The mold properties of the Cu slag mold such as hardness, permeability, compressive strength, and shear strength were evaluated. The model predicted mold properties are validated experimentally. The experimental results show that the mold's hardness, permeability number, compressive strength, and shear strength are 94, 351, 1.31 kg/cm 2 (0.128 MPa), and 0.39 kg/cm 2 (0.038 MPa), respectively. The Cu slag mold properties are benchmarked with commercial-grade silica sand mold. An A356 aluminum alloy casting was made using silica sand and Cu slag molds. The as-cast properties, like hardness, surface roughness, and microstructures, are evaluated and compared between commercial-grade silica sand mold and Cu slag mold casting products, and found a good agreement between them. Therefore, Cu slag molds may be used in the green sand mold casting process. However, its recyclability and sustainability need to be ensured before used it commercially.

metallurgy & metallurgical engineering