High Strength and Shape Memory Spinal Fusion Device for Minimally Invasive Interbody Fusions
Min Liu,Bo Liu,Ziyang Liu,Zhen Yang,Thomas Webster,Huan Zhou,Lei Yang
DOI: https://doi.org/10.2147/ijn.s460339
IF: 7.033
2024-06-01
International Journal of Nanomedicine
Abstract:Min Liu, 1, 2 Bo Liu, 2 Ziyang Liu, 3 Zhen Yang, 2 Thomas J Webster, 4 Huan Zhou, 2 Lei Yang 2 1 School of Materials Science and Engineering, Hebei University of Technology, Tianjin, People's Republic of China; 2 Center for Health Science and Engineering, Hebei Key Laboratory of Biomaterials and Smart Theranostics, School of Health Sciences and Biomedical Engineering, Hebei University of Technology, Tianjin, 300131, People's Republic of China; 3 Department of Orthopedics, Tianjin Hospital, Tianjin, People's Republic of China; 4 School of Engineering, Saveetha University, Chennai, India Correspondence: Huan Zhou; Lei Yang, Center for Health Science and Engineering, School of Health Sciences and Biomedical Engineering, Hebei University of Technology, Tianjin, 300131, People's Republic of China, Email ; Introduction: Lumbar interbody fusion is widely employed for both acute and chronic spinal diseases interventions. However, large incision created during interbody cage implantation may adversely impair spinal tissue and influence postoperative recovery. The aim of this study was to design a shape memory interbody fusion device suitable for small incision implantation. Methods: In this study, we designed and fabricated an intervertebral fusion cage that utilizes near-infrared (NIR) light-responsive shape memory characteristics. This cage was composed of bisphenol A diglycidyl ether, polyether amine D-230, decylamine and iron oxide nanoparticles. A self-hardening calcium phosphate-starch cement (CSC) was injected internally through the injection channel of the cage for healing outcome improvement. Results: The size of the interbody cage is reduced from 22 mm to 8.8 mm to minimize the incision size. Subsequent NIR light irradiation prompted a swift recovery of the cage shape within 5 min at the lesion site. The biocompatibility of the shape memory composite was validated through in vitro MC3T3-E1 cell (osteoblast-like cells) adhesion and proliferation assays and subcutaneous implantation experiments in rats. CSC was injected into the cage, and the relevant results revealed that CSC is uniformly dispersed within the internal space, along with the cage compressive strength increasing from 12 to 20 MPa. Conclusion: The results from this study thus demonstrated that this integrated approach of using a minimally invasive NIR shape memory spinal fusion cage with CSC has potential for lumbar interbody fusion. Keywords: shape memory, interbody fusion cage, NIR responsive, calcium phosphate cement, minimally invasive Fusion surgery is commonly applied as an attempt to alleviate pain and stabilize symptomatic spinal segments. The procedure typically involves inserting an implant, known as a "cage", into the disc space between two vertebrae to stabilize the spine until the bone grows together to achieve interbody fusion. Annually, approximately 210,000 fusions are performed in the United States, with an escalating trend attributed to population aging, lifestyle changes, and other factors. 1 However, current approaches have led to spinal fusion failure rates as high as 35% with an average of 25% of patients requiring another spinal case after just 10–20 years. 2 Over the recent decades, titanium (Ti) and poly-ether-ether-ketone (PEEK) are acknowledged as the primary fusion materials for cage fabrication. In spite of their impressive track record in medical practice, several key limitations of cages are now documented in clinical reports. For example, the mismatched elastic modulus between Ti and vertebra can cause stress shielding, leading to intervertebral settlement and space collapse. Moreover, the surgical implantation required for cage placement between adjacent vertebrae leads to spinal tissue defects and associated risks. This procedure often triggers significant bleeding, with studies reporting transfusion rates of 50–81% for adult spinal fusions, elevating the risk for transfusion reactions, alloimmunization, and infection. 3,4 Surgical-induced tissue defects further complicate postoperative recovery, prolonging hospital stays. Therefore, development of fusion cages adaptable to vertebra mechanical properties and applicable to smaller surgical incision becomes imperative to avert post-surgery complications and expedite patient recovery. Shape memory polymers (SMPs) are a class of programmable smart materials that can change between permanent and temporary shapes. 5 Once the permanent shape is established, altering the conditions (typically based on temperature) to exceed the glass transition temperature ( T g ) or the glass melting temperature ( T m -Abstract Truncated-
pharmacology & pharmacy,nanoscience & nanotechnology