Ultradurable Noncovalent Cross-Linked Hydrogels with Low Hysteresis and Robust Elasticity for Flexible Electronics

Kai Xu,Kaixiang Shen,Jing Yu,Yuxuan Yang,Yuantao Wei,Peiling Lin,Qiang Zhang,Chunhui Xiao,Yanfeng Zhang,Yilong Cheng

DOI: https://doi.org/10.1021/acs.chemmater.2c00093

IF: 10.508

2022-03-17

Chemistry of Materials

Abstract:Development of hydrogel-based flexible electronics with robust elasticity, low hysteresis, and excellent durability is still challenging. Herein, for the first time, B–N coordination was employed as the main driving force to promote gelation by free radical polymerization of acrylamide and 3-acrylamidophenylboronic acid. Owing to the outstanding stability of B–N coordination, the hydrogels could retain their initial stress (>95%) during 500 tension cycles (strain of 200%) with <10% hysteresis. Moreover, the addition of NaCl elevated the mechanical properties (break stress of 0.21 MPa and fracture strain of 1600%) and imparted high electrical conductivity (4.8 S/m) and superior gauge factor (10.2) to the hydrogels. The conductive hydrogels could accurately distinguish various deformations (2.5–200% tensile strain and 1–25 kPa compressive stress) and successively output reliable electrical signals with super durability (1000 tensile cycles with a strain of 100% and 1000 compressive cycles with a stress of 15 kPa). Combined with moderate tissue adhesiveness, the conductive hydrogels can monitor various human activities with constant outputs. This work offers a new solution to integrate high stretchability, robust elasticity, and low hysteresis into noncovalent cross-linked hydrogels, and may show vast potential in the development of flexible electronic devices.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acs.chemmater.2c00093.Additional experimental methods; 1H NMR spectrum of APBA, FT-IR spectra, digital photographs, SEM images, and adhesion strength of the hydrogels; load–unload tests at different strains and the corresponding dissipated energy of the P(AM3–APBA0.06)NaCl1.72 hydrogel; rheology measurement of the hydrogels and mechanical performances (consecutive tensile and compressive cycles) of the P(AM3–APBA0.06)NaCl1.72 hydrogel; and DSC measurements of the hydrogels (PDF)Brightness of a LED varies with tensile strain (Movie S1) (MP4)Brightness of a LED varies with compressive strain (Movie S2) (MP4)Freeze resistance of the P(AM3–APBA0.06) hydrogel (Movie S3) (MP4)Freeze resistance of the P(AM3–APBA0.06)NaCl1.72 hydrogel (Movie S4) (MP4)This article has not yet been cited by other publications.

materials science, multidisciplinary,chemistry, physical