2D nanomaterial–polymer composite: optical and structural properties along with room temperature enhanced dielectric response and magnetic behaviour of graphene oxide doped polyvinylpyrrolidone nanocomposites
Tilak Narayan Ghosh,Amit Kumar Bhunia,Sitangshu S. Pradhan,Rajesh Samui,Satyajit Saha,Subhas Chandra Saha
DOI: https://doi.org/10.1007/s10854-024-12881-1
2024-06-13
Journal of Materials Science Materials in Electronics
Abstract:These days, because of their remarkable potential and mechanical, thermal, and microwave-absorbing qualities, researchers are focusing on graphene and graphene oxide (GO)-polymer composite-based materials for energy storage devices, supercapacitor applications, sensors, and conductive coatings. For the material of GO-polyvinylpyrrolidone (PVP) nanocomposites, the synthesis, characterization, and measurement of room temperature dielectric properties as a function of frequency and magnetic properties have been the main emphasis of this work. A modified Hummers and Offeman method was initially used to produce graphite into graphene oxide. Films of graphene oxide-polyvinylpyrrolidone (GO-PVP) nanocomposites with GO as 15, 30 and 50 wt% were prepared by solution mixing method. Optical absorption, emission, Raman spectrum and FESEM, TEM, XRD, and FT-IR studies was performed on the prepared nanocomposite polymer films. The direct band gap (value tuning from 2.38 to 4.38 eV) properties with semiconducting nature have been observed in the nanocomposites. The Urbach energy has been found to be 0.45, 1.5, 3.55, 3.15, 2 eV for PVP, GO, PVP-GO 15, 30, 50%, respectively. The good emission properties with fine quantum yield and band gap of 2.9 eV, the PVP-GO 50% behave as a better semiconductor nature. In the frequency range of 10 Hz to 10 kHz, and at room temperature, the dielectric characteristics of GO-PVP nanocomposites were measured. Using the measured data, the frequency dependence of the real ( ε ′) and imaginary components of the dielectric constant at room temperature was computed. Up to 500 Hz, the dielectric constant ( ε ′) declined as frequency increased; after that, it remained nearly constant. It is found that the dielectric constant in the investigated nanocomposites increased as the concentration of the GO increased (up to 50%) with very high value (achieved ≈ 2 × 10 4 for the first time). The magnetic properties (M-H measurement) of the GO-PVP composite at room temperature showed hysteresis nature with varying field parameters. The tensile stress of PVP-GO nanocomposites varies from 3535 to 4565 psi, while the tensile strain varies from 42 to 24% with the variation of the GO contents from 15 to 50%.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied