Abstract:This research has demonstrated that SiO 2 impregnation under high vacuum pressure of − 90 kPa can significantly reduce porosity by almost 10%, and improve the mechanical and viscoelastic properties of spruce wood under dry and saturated states. Characterization methods, such as impact test, DMA, SEM, EDS, porosity and SAXS tests were conducted on non-treated and − 90 kPa treated spruce wood samples under dry, saturated and submerged states to analyze the synergistic effect of high vacuum SiO 2 impregnation pressure on wood properties. The results showed that high vacuum impregnation pressure had a significant positive reinforcing effect on wood's properties. It increased the impact resistance of wood under dry and saturated conditions. Additionally, the high vacuum impregnation technique was able to overcome the water-induced softening effect and caused a significant increase in the storage modulus through uniform dispersion of the SiO 2 particles in the wood's vascular structure. Consequently, the impregnation reinforced the wood and ameliorated its capacity to absorb energy. High vacuum impregnation was also able to counteract the plasticizing effect of the water molecules and significantly increased the loss modulus by increasing the internal friction and cohesion of the wood components with the addition of the nanoparticles to the vascular system, which increased the wood's capacity to transform and dissipate energy. Quantitatively and qualitatively, impregnation under a vacuum pressure of − 90 kPa exhibited an effective obstruction of the vascular structure of spruce wood. In all conditions, high vacuum-impregnated samples showed significant enhancements over non-treated samples. This research demonstrated that high vacuum SiO 2 impregnation is an effective wood processing technique. Multiple materials and applications could benefit from this research wherein high strain-rate deformations are expected to occur or when simultaneous elastic behaviour of wood and its damping energy is needed. This study could also pave the way for research on the synergistic effect of SiO 2 impregnation and water absorption on the viscoelastic behaviour of wood.

Effect of unilateral surface-densification process on wood-surface coating properties

High-pressure Densification and Hydrophobic Coating for Enhancing the Mechanical Properties and Dimensional Stability of Soft Poplar Wood Boards

The study of physico-mechanical properties of SiO2-impregnated wood under dry and saturated conditions

High-Pressure Treatment of Chinese Fir Wood: Effect on Density, Mechanical Properties, Humidity-Related Moisture Migration, and Dimensional Stability

High-Pressure Treatment Effects on Density Profile, Surface Roughness, Hardness, and Abrasion Resistance of Paulownia Wood Boards

A Review on the Effect of Wood Surface Modification on Paint Film Adhesion Properties

Mayo Clinic Proceedings celebrates 70th year of publication.

Enhanced paint adhesion of puffed wood-based metal composites via surface treatment with silane coupling agent

Effect of Photoinitiator Concentration and Film Thickness on the Properties of UV-Curable Self-Matting Coating for Wood-Based Panels

Effect of superheated steam pressure on the physical and mechanical properties of sandwich-densified wood

Effects of the Surface Roughness of Six Wood Species for Furniture Production on the Wettability and Bonding Quality of Coating

Preparation and Properties of a Novel Cross-Linked Network Waterborne Polyurethane for Wood Lacquer

Cyclic AMP increases the concentration of insulin receptors in cultured fibroblasts and lymphocytes.

Improvement of decorative texture effects, thermal stability, and mechanical properties of Pinus massoniana using a combined dyeing and superhydrophobic modification method

“Late” recovery of the right ear dichotic score following cerebrovascular accident: A case report

Effective strategy for fabricating surface impregnated and unilaterally densified wood with furfuryl alcohol/flame retardants for enhanced mechanical performance and flame retardancy

Creation of a high strength, hydrophobic and fireproof surface on wood by polyamide acid under mild and simple conditions

Measurement of Mechanical Properties of Multilayer Waterborne Coatings on Wood by Nanoindentation

Enhancement of Wood Coating Properties by Adding Silica Sol to UV-Curable Waterborne Acrylics

The Effect of Antibacterial and Waterproof Coating Prepared From Hexadecyltrimethoxysilane and Nano-Titanium Dioxide on Wood Properties

Towards high performance wood composites through interface customization with cellulose-based adhesive