Polymer/carbon Nanotube Composites: Challenges and Opportunities
Satish Kumar,Tao Liu,T. V. Sreekumar,Tetsuya Uchida,Xiefei Zhang,Young Bin Park
2004-01-01
Abstract:Due to their exceptional mechanical, physical, therma l, optical, and electrical properties , carbon nanotubes are being dispersed in polymers using variety of approaches. These polymer/carbon nanotube composites are being used to make film, fibers, and bulk composites with enhanced strength, stiffness, and electrical conductivity. Polymer/ carbon nanotube composites also exhibit reduced thermal shrinkage as well enhanced solvent resistance. Single wall carbon nanotubes have high specific surface area, which can be further increased in activated carbon/single wall carbon nanotube composite. Such composite systems are promising candidates for supercapacitor applications. While single wall carbon nanotubes offer outstanding opportunities in materials development, many of the predicted properties can be achieved only if nanotubes are well dispersed, exfoliated, and oriented in the polymer systems of interest. INTRODUCTION Carbon fibers (typical diameter 7 – 10 μm) for composite applications were developed during 1960s, while the development of carbon nano fibers (typical outer diameter 50 – 200 nm) dates back to 1980s.1 The existence of carbon nanotubes was recognized in 1990s which are now being produced with multiwalls or a single wall. While carbon fibers, carbon nano fibers, 3 multiwall carbon nanotubes (MWNT), as well as single wall carbon nanotubes (SWNT) are being used for reinforcing polymer matrices , SWNTs are sometimes heralded to be the ultimate in carbon reinforcement. Tremendous amount of work (according to the web of science data base, over 7500 research papers have so far been published on carbon nanotubes) has been done in producing, characterizing, and processing carbon nanotubes over the last decade. However, the production and processing technology , particularly for the single wall carbon nanotubes is still in its infancy. Currently SWNTs are expensive ($500/g) and can only be produced with a diameter (typically 0.7 to 1.4 nm) and chirality distribution. As produced tubes, typically contain as much as 30 wt% catalytic impurity. In addition, one third of the nanotubes in a given batch are expected to be metallic and the other two thirds are semi-conducting. It is expected that SWNT applications will increase dramatically if they can be produced with controlled diameter and chirality and at a reasonable cost. Carbon nanotubes are being dispersed in polymer matrices using melt processing, solution processing, or insitu polymerization. Property enhancement include strength, stiffness, thermal stability, solvent resistance, glass transition temperature, electrical conductivity, reduced thermal shrinkage as well as optical anisotropy. The presence of SWNTs can also influence polymer crystallization. In addition carbon nanotubes are over 10 times more resistance to the electron radiation than polyethylene and about 103 times more resistance than highly radiation resistance rigid-rod polymers such as poly (p -phenylene benzobisoxazole). Typical SWNT properties and potential applications of their composites are given in Table 1.