Effects of β-cooling rates on microstructural characteristics and hardness of Ti–5Al–5Mo–5V–3Cr–1Fe metastable β Ti alloy

Zhiying Zheng,Linjiang Chai,Zhihao Li,Weijiu Huang,Lin Tian,Yongfeng Wang,Liangliang Liu

DOI: https://doi.org/10.1016/j.matchemphys.2021.125318

IF: 4.778

2022-01-01

Materials Chemistry and Physics

Abstract:A typical metastable β Ti alloy (Ti–5Al–5Mo–5V–3Cr–1Fe alloy) was β-solution treated (890 °C for 10 min) and then cooled at different rates (in water (WC), air (AC) and furnace (FC)). To clarify specific effects of β-cooling rates, multiple characterization techniques were jointly utilized to reveal their microstructural and orientation characteristics in detail, with hardnesses also measured and correlated with specific microstructures. Results show that both the WC and the AC specimens are mainly comprised of recrystallized β grains with no α phase, while the FC specimen consists of coarse equiaxed β grains, intragranular acicular α phase (width ∼48 nm) and grain boundary α phase. The Burgers orientation relationship is strictly obeyed during β→α transformation in the FC specimen. When adjacent β grains share a common <110> axis, the boundary α phase maintains such orientation relationship with both of them. Compared to the as-received specimen (428 ± 9 HV), the WC (309 ± 5 HV) and the AC specimens (297±3HV) are softened, which can be attributed to the coarsened β grains as well as the disappearance of α phase and deformed structures. For the FC specimen, dense fine α precipitates appear inside β grains during slow cooling, leading to increased hardness (444 ± 9 HV).

materials science, multidisciplinary