Improving the Critical Temperature of MgB2 Superconducting Metamaterials Induced by Electroluminescence

Zhiwei Zhang,Shuo Tao,Guowei Chen,Xiaopeng Zhao

DOI: https://doi.org/10.1007/s10948-015-3344-7

2016-01-12

Journal of Superconductivity and Novel Magnetism

Abstract:The MgB2 superconductor was doped with electroluminescent Y2O3:Eu, to synthesise a superconducting metamaterial. The temperature dependence of the resistivity of the superconductor indicates that the critical temperature (TC) of samples decreases when increasing the amount of doped Y 2O3 nanorods, due to impurity (Y 2O3, MgO and YB 4). However, the TC of the samples increase with increasing amount of doped Y 2O3:Eu 3+ nanorods, which are opposite to doped Y 2O3 nanorods. Moreover, the transition temperature of the sample doped with 8 wt % Y 2O3:Eu 3+nanorods is higher than those of doped and pure MgB 2. The TC of the sample doped with 8 wt % Y 2O3:Eu 3+ nanorods is 1.15 K higher than that of the sample doped with 8 wt % Y 2O3. The TC of sample doped with 8 wt% Y 2O3:Eu 3+ is 0.4 K higher than that of pure MgB 2. Results indicate that doping electroluminescent materials into MgB 2 increases the transition temperature; this novel strategy may also be applicable to other superconductors.

physics, condensed matter, applied