Highly selective oxidation of styrene into benzaldehyde over nano CeWO x composite confined in N-doped carbon under solvent-free conditions

Binxiong Guang,Weijia Pu,Yiwei Zhang,Wei Zhang,Yahui Xiao,Yong Liu

DOI: https://doi.org/10.2139/ssrn.4408529

IF: 4.6

2023-06-17

Molecular Catalysis

Abstract:Highly selective oxidation of styrene into benzaldehyde with molecular oxygen under solvent-free conditions still remains a great challenge. Herein, Ce-modified heteropolyacid-based poly(ionic liquid)s were prepared as precursors followed by carbonization to obtain nano CeWO x composite confined in N-doped carbon (CeWO x @NC). Then, the as-prepared catalysts were further characterized by FT-IR, TG, XRD, XPS, BET, SEM, TEM-EDS and H 2 -TPR to discuss the relationship between the structure and performance. The nano CeWO x composite with a mixed valence state of W 4+ and W 6+ was formed and well dispersed in the N-doped carbon. Moreover, the valence ratio of W 4+ to W 6+ , redox capacity and oxygen vacancies could be tailored by carbonization temperature and incorporation of Ce, which was strongly correlated with the catalytic performance of CeWO x @NC catalysts. Benefited from that, the CeWO x @NC800 catalyst displays outstanding catalytic performance for solvent-free oxidation of styrene into benzaldehyde with styrene conversion of 45.1%, benzaldehyde selectivity of 89.2% and TOF of 310.1 h −1 at the optimum reaction conditions. Furthermore, the catalyst has shown robust stability and reusability.

chemistry, physical