One-pot synthesis of siliceous ferrihydrite−coated halloysite nanorods in alkaline medium: Structure, properties and cadmium adsorption performance

Ying Li,Xingzhong Yuan,Xian Guan,Jing Bai,Hou Wang

DOI: https://doi.org/10.1016/j.jcis.2023.01.010

IF: 9.9

2023-01-08

Journal of Colloid and Interface Science

Abstract:The application of amorphous ferrihydrite (Fh) for Cd(II) removal is restricted by its unstable and easily transformable nature. Although doping with silicates stabilized ferrihydrite, its product siliceous ferrihydrite (SiFh) again suffered from the disadvantage of spontaneous agglomeration. Herein, ferrihydrite was hybridized with halloysite nanotubes (HNTs) to prepare a novel siliceous ferrihydrite−coated halloysite nanorods () in alkaline medium, to break through the current barriers. The characterization results showed that could simultaneously overcome the defects of easy phase transformation of ferrihydrite and easy aggregation of SiFh nanoparticles (NPs). Meanwhile, the optimal 40 with halloysite content of 40% formed a well-developed mesoporous structure and exhibited the desired surface properties: a high specific surface area of 303.4 m 2 /g, an isoelectric point as low as pH iep = 4.5, and rich functional Fe−OH groups. The formation mechanism of such excellent sturcture–properties of 40 were mainly attributed to two factors: the generation of smaller (∼5 nm) SiFh NPs induced by the integration of halloysite-derived SiO 4 4- into ferrihydrite, and the dispersion of SiFh NPs on clay nanotubes. Furthermore, the adsorption capacity of 40 for Cd(II) was up to 137.8 mg/g at 30 °C and pH 6, which was much higher than that of aggregated ferrihydrite (11.2 mg/g), halloysite (18.8 mg/g) and goethite (49.4 mg/g). The adsorption thermodynamics study revealed the adsorption of Cd(II) on 40 was clearly chemisorption with a (ΔH ads ) q of 43.3 kJ/mol. Characterization results of XPS and FTIR confirmed that the rich Fe−OH groups on 40 was the main adsorption sites, and Cd(II) was specifically adsorbed by inner-sphere surface complexation. In addition, 40 had application potential in the mixed-metal wastewaters treatment. Cyclic regeneration experiments showed that 40 had good regeneration performance and could be reused many times.

chemistry, physical