Green synthesis of bimetallic Se@TiO2NPs and their formulation into biopolymers and their utilization as antimicrobial, anti-diabetic, antioxidant, and healing agent in vitro
Mohammed Ibrahim Alghonaim,Sulaiman A. Alsalamah,Abeer Mahmoud Mohammad,Tarek M. Abdelghany
DOI: https://doi.org/10.1007/s13399-024-05451-2
IF: 4.05
2024-02-28
Biomass Conversion and Biorefinery
Abstract:A promising combination of two nanoparticles that typically exhibit synergetic behaviors is called bimetallic nanoparticles. The synthesis of bimetallic selenium and titanium oxide nanoparticles (Se@TiO 2 NPs) in the current work was carried out using green creator Talaromyces pinophilus . A green technique was employed to create formulated nanoparticles into biopolymers (nanocomposite) using carboxymethylcellulose and starch. Se@TiO 2 NPs and nanocomposite characteristics were carried out via physicochemical including FITR and XRD and topographical characterization including FESEM and HRTEM. Se@TiO 2 NPs diameters were 25 nm and the nanocomposite was noticed as a nano matrix and was found to have confirmed nanostructures. More inhibitory action was observed using nanocomposite than Se@TiO 2 NPs against Staphylococcus aureus , Salmonella typhi , Enterococcus faecalis , Candida albicans , Aspergillus flavus , and Mucor circinelloid with inhibition zones of 21, 23, 25, 29, 16, and 18 mm using nanocomposite, while it was 19, 21, 24, 26, 13, and 12 mm using Se@TiO 2 NPs, respectively. Nanocomposite revealed low values of MIC (62.5, 31.25, and 7.8 μg/mL) in contrast to the MIC values of Se@TiO 2 NPs (125, 62.5, and 15.62 μg/mL) toward S. aureus , S. typhi , and C. albicans , respectively. DPPH scavenging % and α-amylase inhibition % were more affected by nanocomposite (IC 50 , 41.40 μg/mL and 8.82 μg/mL, respectively) than Se@TiO 2 NPs (IC 50 , 103.41 μg/mL and IC 50 , 12.96 μg/mL, respectively). Moreover, healing properties of nanocomposite were better than Se@TiO 2 NPs.
energy & fuels,engineering, chemical