Tribological performance of recyclable oil-soluble magnetic MXene as efficient lubricant additives under boundary lubrication conditions

Xiaoyu Wang,Yan Zhao,Bo Dai,Qianfang Sun,Xiaobo Wang,Wenjing Lou,Jun Yang

DOI: https://doi.org/10.1016/j.triboint.2024.110427

IF: 5.62

2024-12-01

Tribology International

Abstract:The design and synthesis of efficient lubricant additives based on MXene, an emerging two-dimensional layered material, have attracted increasing attention. In this study, a recyclable oil-soluble magnetic MXene (C 12 PA-MXene@Fe 3 O 4 ) was synthesized through in-situ loading Fe 3 O 4 nanoparticles on MXene nanosheets, and subsequently modified with dodecylphosphonic acid. The tribological performance of the synthesized additive was investigated under varying boundary lubrication conditions. The results show that the addition of 0.5 wt% C 12 PA-MXene@Fe 3 O 4 reduced the average friction coefficient (AFC) and the wear volume by 14.8% and 95.0%, respectively, when compared to the base oil. The pronounced tribological performance of C 12 PA-MXene@Fe 3 O 4 is attributed to its good dispersibility and the synergistic effect of MXene nanosheets and Fe 3 O 4 nanoparticles. The MXene nanosheets work as carriers for Fe 3 O 4 nanoparticles, preventing their aggregation. Moreover, the Fe 3 O 4 nanoparticles, when loaded on MXene nanosheets, facilitate the sliding of MXene layers by expanding the interlayer spacing. After the tribological test, a continuous and relatively smooth tribofilm forms on the surface, with a thickness ranging from 38 to 80 nm, which is composed of phosphate ions, titanium oxide, and iron oxides. The tribofilm prevents the direct contact of rubbing surfaces, contributing to the superior anti-wear performance.

engineering, mechanical