Development and characterization of highly conductive hybrid Moringa oleifera husk biocarbon and grape pulp cobalt oxide polyvinyl alcohol composites for microwave shielding
S. Kavitha,B. Chinthamani,K. A. Indu Sailaja
DOI: https://doi.org/10.1007/s13399-024-06212-x
IF: 4.05
2024-10-12
Biomass Conversion and Biorefinery
Abstract:This study focuses on the fabrication and characterization of highly conductive polyvinyl alcohol (PVA) composites enhanced with biocarbon derived from Moringa oleifera husk and cobalt oxide extracted from grape fruit pulp, aimed at improving microwave shielding and electromagnetic interference (EMI) properties. The main objective is to study how the cobalt oxide extracted from grape fruit pulp modifies the property of composites. The PVA matrix, chosen for its process-ability and structural stability, was combined with biocarbon and cobalt oxide using a solvent casting method to form hybrid composites with enhanced electrical conductivity and EMI shielding capabilities. Biocarbon was prepared through a three-stage pyrolysis process of Moringa oleifera husk, while cobalt oxide was synthesized from grape pulp extract through a series of chemical reactions and calcination. The hybrid PVA composites demonstrated significant improvements in EMI shielding and magnetic properties, particularly for specimen P31, which contains 5 vol.% of both biocarbon and cobalt oxide fillers. P31 achieved the highest EMI shielding effectiveness, with values ranging from 26.3 dB at 8 GHz to 63.0 dB at 20 GHz, due to the synergistic effects of cobalt's magnetic properties and biocarbon's conductivity, enabling enhanced electromagnetic attenuation through reflection, absorption, and multiple internal reflections. It also exhibited the highest magnetic properties, with values increasing from 4.4 at 8 GHz to 6.8 at 20 GHz, attributed to a higher magnetic moment and improved magnetic permeability due to the uniform dispersion of cobalt oxide within the matrix. Conversely, specimen P11, which contains 5 vol.% biocarbon and 1 vol.% cobalt oxide, showed superior mechanical properties, including the highest tensile strength of 56 MPa and tear strength of 207 MPa. This is due to the effective reinforcement provided by the biochar and the strong interfacial bonding between the PVA matrix and the hybrid fillers. SEM analysis revealed that P11 has a uniform dispersion of fillers, leading to fewer defects and better stress transfer, while specimens with higher filler content, such as P31, exhibited some agglomeration, which can act as stress concentrators. The study highlights the potential of these hybrid composites for applications requiring robust EMI shielding, magnetic properties, and structural integrity.
energy & fuels,engineering, chemical