Abstract:Bubble growth processes are highly influenced by the elongational viscosity of the blowing agent-loaded polymer melt. Therefore, the elongational viscosity is an important parameter for the development of new polymers for foaming applications, as well as for the prediction of bubble growth processes. Thus, knowledge of the initial expansion and deformation behavior in dependency on the polymer, the blowing agent concentration, and the process conditions is necessary. This study presents a novel method for the in-line observation and analysis of the initial expansion and deformation behavior within the bead foam extrusion process. For this purpose, nitrogen as the blowing agent was injected into the polymer melt (PS and PLA) during the extrusion process. The in-line observation system consists of a borescope equipped with a camera, which was integrated into the water box of an underwater pelletizer. The camera is controlled by a developed trigger by means of angular step signal analysis of a rotary encoder on the cutter shaft of the underwater pelletizer. Thus, images can be taken at any time during the foaming process depending on the cutter position to the die outlet. It is shown that the developed method provides reliable results and that the differences of the initial expansion and deformation behavior during bubble growth can be analyzed in-line in dependency on real foaming process conditions and the type of polymer used.
What problem does this paper attempt to address?
The problem that this paper attempts to solve is how to measure and analyze the strain rate and deformation rate on which bubble growth depends during the foam formation process online. Specifically, the research focuses on how to observe and analyze the initial expansion and deformation behaviors in real - time during the foam extrusion process, and these behaviors are affected by the type of polymer used, the concentration of the foaming agent, and the process conditions. By developing a new online observation method, the author aims to provide reliable data to describe the instantaneous tensile deformation behavior at the bubble wall and further understand the viscosity change during the bubble growth process.
### Research Background
Foamed polymer is a two - phase system composed of a matrix material (polymer phase) and a foaming agent (gas phase). Due to its high gas content and honeycomb structure, foamed polymer has the characteristics of low density, high heat and sound insulation capabilities, and high compressibility. When processing polymer melts containing a foaming agent, gas can be generated through chemical reactions or physical phase changes. Physical foaming agents (such as nitrogen used in this study) are injected into the polymer melt under high pressure to form a two - phase system. Subsequently, the nucleation of nuclei is triggered by the decrease in pressure, and bubbles begin to form and continue to grow until the bubble growth is inhibited due to the increase in melt viscosity caused by cooling.
### Three Stages of Bubble Growth
1. **Viscosity - Controlled Period**: In the early stage of bubble growth, hydrodynamic forces are dominant, mainly the pressure difference between the internal pressure of the bubble and the surrounding melt pressure. At this time, the amount of foaming agent diffusing from the polymer melt to the gas phase is very small, and the growth rate of the bubble mainly depends on the extensional viscosity of the polymer melt into which the foaming agent is blown.
2. **Transition Period**: The pressure inside the bubble drops rapidly and approaches the ambient (or melt) pressure. As the concentration gradient between the inside of the bubble and the polymer melt increases, the foaming agent begins to enter the gas phase through diffusion.
3. **Diffusion - Controlled Period**: The main driving force for bubble growth is the diffusive mass flow of the foaming agent from the polymer melt to the bubble. In these three stages, the extensional viscosity at the bubble wall must be less than the driving force inside the bubble to overcome the deformation resistance.
### Research Methods
To achieve this goal, the author has developed an online observation and analysis method, specifically including:
- **Material Selection**: Amorphous polystyrene (PS) and semi - crystalline polylactic acid (PLA) are used as research objects.
- **Rheological Property Characterization**: A rotational rheometer and a Sentmanat extensional rheometer are used to measure the rheological properties under shear deformation and uniaxial extensional deformation respectively.
- **Online Observation System**: An endoscope with a camera is integrated in the water tank of the underwater pelletizer, and the shooting timing of the camera is controlled by a rotary encoder, so as to capture images at different cutting positions.
- **Experimental Parameters**: Different extrusion temperatures, screw rotation speeds, and foaming agent injection amounts are set to study the initial expansion and deformation behaviors under different conditions.
### Conclusions
Through this method, the author is able to observe and analyze the overall expansion and instantaneous tensile deformation behavior at the bubble wall in real - time during the actual foam formation process for the first time. This provides important data support for describing the viscosity dependence during the bubble growth process and is helpful for developing more accurate bubble growth models.