Influence of sulphonation on Al-MCM-41 catalyst for effective bio-glycerol conversion to Solketal
Balakrishna Matkala,Sasikumar Boggala,Srinivas Basavaraju,V.S. Sarma Akella,Hari Padmasri Aytam
DOI: https://doi.org/10.1016/j.micromeso.2023.112830
IF: 5.876
2023-09-23
Microporous and Mesoporous Materials
Abstract:Al-MCM-41 and sulphate modified Al-MCM-41 catalysts with variable sulphate loadings (0.25-1SAM) were synthesized through sol-gel and impregnation techniques respectively for the transformation of glycerol into solketal, a fuel additive via acetalization reaction. The mesoporous structure, surface morphologies, composition and porosity of the prepared catalysts were subjected to characterization by Low angle XRD, SEM-EDAX, TEM, FT-IR, XPS and BET-surface area studies. The strength and quantification of acid sites were obtained from TPD of NH 3 . Pyridine-adsorbed FTIR and 27 Al MAS NMR data distinguished Lewis and Brønsted acid sites present on the catalysts. Among the synthesized catalysts, 1 N sulphated Al-MCM-41 was a better catalyst that promotes a higher solketal formation rate of 23.5 mmol h −1 g cat −1 by the acetalization of glycerol. This is much higher in comparison to 4 times lesser activity of 6.1 mmol h −1 gcat −1 exhibited by the parent Al-MCM-41. This catalyst further showed consistent activity and reusability up to 5 cycles. Large surface area, total acidity, strong Lewis acid sites, compatible surface characteristics of 1 N sulphated Al-MCM-41 endorse the higher acetalization activity of the catalyst. As a result, these parameters have been regarded as crucial considerations in designing a better catalyst in the effective conversion of glycerol to solketal.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology, applied