Abstract:NH4Cl corrosion failure often occurs in the overhead systems of hydrotreaters, and this failure is always accompanied by the appearance of H2S. A combination of electrochemical and surface spectroscopic (SEM/EDS, AFM, XRD) techniques was used to investigate the effect of different factors, including the surface roughness, temperature, dissolved oxygen, pH and H2S concentration, on the corrosion behavior of carbon steel in an NH4Cl environment with the presence of H2S. The effect of H2S concentrations (at the ppm level) on the corrosion behavior of carbon steel was systematically revealed. The experimental results clearly indicated that the corrosion rate reached a minimum value at 10 ppm H2S. The steel surface was covered by a uniform corrosion product film in a 10 ppm H2S environment, and the corrosion product film was tight and protective. The ammonia from NH4Cl helped maintaining the protectiveness of the corrosion films in this environment. Dissolved oxygen mainly accelerated the cathodic reaction. The cathodic limiting current density increased with increasing temperature, and the anodic branch polarization curves were similar at different temperatures. The anodic current density decreased as the pH decreased, and the cathodic current density increased as the pH decreased. The absolute surface roughness (R (a)) of carbon steel increased from 132.856 nm at 72 h to 153.973 nm at 144 h, and the rougher surface resulted in a higher corrosion rate. The critical innovation in this research was that multiple influential factors were revealed in the NH4Cl environment with the presence of H2S.

A time-resolved study of PbCl 2 -induced corrosion of low-alloyed steel in the presence of water vapour at 400 °C

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Corrosion Behavior of Carbon Steel in LiCl/H2O Mixtures

Molecular Dynamics Simulation of Reinforcing Steel Corrosion when Subjected to Both Chloride Attack and Mechanical Loading

Effect of KCl on high‐temperature corrosion of low‐alloyed steel under low oxygen partial pressure

Passivation and Depassivation of HPB335 Carbon Steel in Simulated Concrete Pore Solution

Initiation and propagation of pitting and crevice corrosion of hydrogen-containing passive films on X70 micro-alloyed steel

A Study on the Corrosion Behavior of Carbon Steel Exposed to a H2S-Containing NH4Cl Medium

Shifts in the Binding Energies of Cr2p, Fe2p and O1s electrons of Alloy Oxide Films in the Presence of Pb During High- Temperature Water Corrosion

Effect of water vapor content on the corrosion mechanism of HR3C in simulated oxy-coal combustion environment

Chlorine-induced High-Temperature Corrosion of the Pt-modified Aluminide Coating in Simulated Marine Environment

Effect of H3bo3 on Corrosion in 0.01 M Nacl Solution of the Interface Between Low Alloy Steel A508 and Alloy 52 M

A study of the influence of chloride ion concentration on the corrosion behavior of carbon steel in phosphate high-temperature boiler water chemistries

Hydrogen Insertion into Complex-Phase High-Strength Steel during Atmospheric Corrosion at Low Relative Humidity

The effect of acidification on hydrogen uptake and corrosion resistance of advanced high-strength steels

Hydrogen-enhanced oxidation of ferrite phase in stainless steel cladding and the contribution to stress corrosion cracking in deaerated high temperature water

Corrosion Behavior and Mechanism of Ni-based Alloys Hastelloy C2000 and Inconel 740 in Chloride-Containing Supercritical Water Oxidation

Influence of Alloying Element on Corrosion Behavior of Hastelloy C-276 in Supercritical Water

Effect of Dissolved Oxygen on Pitting Corrosion Behavior of Low-Alloy Steel under Hydrostatic Pressure

Study on effect of chloride ions on corrosion behavior of reinforcing steel in simulated polluted concrete pore solutions by scanning micro-reference electrode technique

Direct observation of pitting corrosion evolutions on carbon steel surfaces at the nano-to-micro- scales