Ag2O/TiO2 hollow microsphere heterostructures with exposed high-energy {001} crystal facets and high photocatalytic activities
Tao Wang,Huan Xiao,Yang Gao,Jiahui Xu,Zhengmei Zhang,Haiqin Bian,Tianyi Sun
DOI: https://doi.org/10.1007/s10854-020-03697-w
2020-05-30
Abstract:In this paper, one-step hydrothermal method was used to prepare the graded titanium dioxide hollow microspheres, and the {001} crystal plane was exposed. The silver oxide nanoparticles were deposited on the exposed crystal face of titanium dioxide by wet chemical coprecipitation to form Ag<sub>2</sub>O/TiO<sub>2</sub> composite material. The samples were characterized by X-ray diffraction, scanning electron microscopy, transmission electron microscopy, nitrogen adsorption–desorption (BET), and so on. The degradation abilities of Ag<sub>2</sub>O/TiO<sub>2</sub> composite materials with different molar ratios to rhodamine B were studied under UV–Vis irradiation. And then the mechanism of photocatalytic degradation was analyzed. The experimental results showed that when the molar ratio of titanium dioxide to silver nitrate was 4:1, the degradation effect was best, and the degradation rate reached 95.4% in 80 min. This outstanding photochemical catalysis performance was mainly due to good cooperation, including exposure of specific crystal planes of TiO<sub>2</sub> hollow microspheres and highly scattered Ag<sub>2</sub>O nanoparticles, and the p–n heterostructure between Ag<sub>2</sub>O and TiO<sub>2</sub> will induce efficient charge separation efficiency.