Influence of mixed-phase TiO2 on the activity of adsorption-plasma photocatalysis for total oxidation of toluene

Zhiping Ye,Zhen Ye,Anton Nikiforov,Jun Chen,Wu Zhou,Jianmeng Chen,Guanjie Wang,Yufen Zhang

DOI: https://doi.org/10.1016/j.cej.2020.126280

IF: 15.1

2021-03-01

Chemical Engineering Journal

Abstract:Herein, the effects of different crystalline phases of TiO2 on the adsorption-plasma photocatalytic oxidation of toluene were investigated. First, photocatalysts loaded on a molecular sieve (MS) were characterised and the catalytic performance of toluene abatement was evaluated in a plasma system. The COX yield of the pure anatase (An) sample outperformed other samples in the adsorption-plasma photocatalytic oxidation process, especially for CO2 yield (69.1%). It was revealed that the highest space-time-yield of 2.35 gco2/Lcat•h was also achieved using plasma-An/MS. However, the highest total toluene abatement (99.5%) was achieved in the plasma-P25/MS system. The plasma-generated UV flux only played a minor role in photocatalyst activation because of the very low UV flux of 2.7 μW/cm2 generated by discharge. For the degradation pathway, compared with the plasma-MS system, byproducts of 1,3-Butadiyne (C4H2), guanidine, methyl- (C2H7N3) did not exist in the TiO2-assisted system, indicating a difference in the toluene degradation pathway. There were no obvious effects of different TiO2 samples on organic byproducts generation, and almost a complete mineralisation of all byproducts was observed after 30 min of treatment, with the exception of ethylamine (C2H7N) and acetaldehyde (C2H4O). Finally, a cycled adsorption-plasma study was conducted to reveal the sustainability of the process. A partial deactivation of plasma-An/MS with less than 7% decrease in CO2 selectivity after 7 cycles was revealed, which is a promising result for use in possible industrial applications.

engineering, chemical, environmental

What problem does this paper attempt to address?

The paper aims to investigate the role of different crystal phases of titanium dioxide (TiO₂) in the adsorption and plasma photocatalytic oxidation of toluene. Specifically, the study focuses on the following aspects:

1. **Catalyst Performance**: By loading different crystal phases of TiO₂ onto molecular sieves, the effectiveness of toluene removal in a plasma system is evaluated.
2. **Toluene Removal Efficiency**: The performance of pure anatase (An), rutile (Ru), commercial P25, and mechanical mixtures (3An:1Ru) in the plasma photocatalytic oxidation process is compared.
3. **Intermediate Product Formation**: The impact of different TiO₂ crystal phases on the formation of organic by-products is studied, and changes in the toluene degradation pathway are explored.
4. **Role of UV Photons**: The role of UV photons generated by the plasma in the activation of the catalyst is examined.
5. **Process Sustainability**: The sustainability of the process is verified through cyclic experiments, particularly focusing on the activity changes of the catalyst after multiple cycles.

The results show that the pure anatase (An) sample exhibited the highest carbon dioxide yield (69.1%) during the plasma photocatalytic oxidation process and achieved the highest space-time yield (2.35 gCO₂/Lcat·h). However, the highest toluene removal efficiency (99.5%) was achieved in the plasma-P25 system. Additionally, the study found that the role of UV photons generated by the plasma in catalyst activation was limited, while different crystal phases of TiO₂ had a significant impact on the toluene degradation pathway.