Crystallization ability of glasses based on slags from the joint smelting of silicate nickel and copper pyrite ores

Alexander Klyushnikov,Roza Gulyaeva,Svetlana Sergeeva,Sergey Agafonov,Lyubov Cherepanova

DOI: https://doi.org/10.1007/s10973-024-13179-4

IF: 4.755

2024-05-23

Journal of Thermal Analysis and Calorimetry

Abstract:In order to substantiate the possibility of obtaining glass–ceramics from glasses based on slags from the joint smelting of silicate nickel and copper pyrite ores, the crystallization ability of model samples (particle size < 0.1 mm) that are close in composition and structure to real prototypes was evaluated. Using the methods of differential scanning calorimetry (5–20 °C·min −1 heating rate) and X-ray powder diffraction, it was established that in an inert atmosphere, crystallization is accompanied by the formation of products, the crystalline part (46.6–71.6 mass%) of which is represented by associations of pyroxenes and anorthite. The primary crystallizing phase is pyroxene. The transition from iron-free to iron-containing sample leads to a change in the composition of pyroxene from enstatite to pigeonite, a shift in the range of formation of these associations from 826–1018 to 728–874 °C, and additional (966–1068 °C) formation of silica. Kinetic analysis (Ozawa–Flynn–Wall and multi-variate nonlinear regression methods) showed consecutive bulk nucleation of pyroxenes and anorthite with the formation of two- and one-dimensional nuclei by a chain mechanism, passing into diffusion-controlled two- and three-dimensional crystal growth. The activation energy of enstatite nucleation (671 kJ·mol −1 ) is significantly higher than for pigeonite (418 kJ·mol −1 ), and for crystal growth (444 and 534 kJ·mol −1 , respectively), the reverse relationship is noted. Pyroxenes promote the heterogeneous nucleation of anorthite. The activation threshold for the release of the latter in an iron-free sample (220 kJ·mol −1 ) is three times higher than in an iron-containing one (76 kJ·mol −1 ). The formation of two- and one-dimensional silica nuclei in the bulk of glass is synchronized with their two-dimensional growth under conditions of diffusion deceleration. The results obtained can be used in the development of technologies for producing glass–ceramics from various types of technogenic and mineral raw materials.

chemistry, physical, analytical,thermodynamics