Abstract:Two acrylate monomers with six-member cyclic ortho ester groups, i.e., 2-(1,3-dioxan-2-yloxy)ethyl acrylate (DEA) and 2-(5,5-dimethyl-1,3-dioxan-2-yloxy) ethyl acrylate (DMDEA), were synthesized. These two monomers were copolymerized with an oligo(ethylene glycol) acrylate (OEGA) under atom transfer radical polymerization conditions to afford two series of thermoresponsive copolymers, poly(DEA-co-OEGA)s and poly(DMDEA-co-OEGA)s. All the copolymers were soluble in water to form transparent solutions at low temperature, however, some of them exhibited association behaviors below the cloud point (CP) as evidenced by (HNMR)-H-1, dynamic light scattering (DLS) and fluorescence method. The aggregation tendency of the copolymers depends on their composition as well as the structure of the ortho ester units. With a similar composition, poly(DMDEA-co-OEGA) showed a stronger aggregation tendency than poly(DEA-co-OEGA). In addition, increasing molar content of the ortho ester units in a copolymer promoted its aggregation in water. Thermally induced phase transitions of these copolymers were studied by various methods including turbidimetry, temperature-dependent (HNMR)-H-1, DLS, and microscopy. The results indicate that CP of the copolymers increased with increasing the content of OEGA units, but the changing behaviors of CP were rather different for two types of copolymers, which can be ascribed to the difference in hydrophobicity of the ortho ester units. Little hysteresis was observed for the copolymers with more OEGA units while those with more alto ester units showed significant hysteresis probably due to the hydrophobic character of the ortho ester. The formation of coacervate droplets above CP reveals that the copolymers underwent a liquid liquid phase separation upon heating. pH-dependent hydrolyses of the copolymers were studied by turbidimetry and H-1 NMR methods. The hydrolysis rate depends greatly on pH and the hydrophilic/hydrophobic balance of the copolymers: lower pH and more hydrophilic character resulted in a faster hydrolysis rate. Finally, this type of acid-labile thermoresponsive copolymers and the acid-catalyzed hydrolysis products have low cytotoxicity.

Facile synthesis of acrylamide derivative copolymers with side urethane groups for systematic variation of the thermoresponsive behavior

Aqueous Synthesis of Upper Critical Solution Temperature and Lower Critical Solution Temperature Copolymers through Combination of Hydrogen‐Donors and Hydrogen‐Acceptors

Control of the temperature responsiveness of poly(N-isopropylacrylamide-co-2-hydroxyethyl methacrylate) copolymer using ultrasonic irradiation

Thermoresponsive Hyperbranched Polymers Via in Situ RAFT Copolymerization of Peg‐based Monomethacrylate and Dimethacrylate Monomers

Making Hydrophilic Polymers Thermoresponsive: The Upper Critical Solution Temperature of Copolymers of Acrylamide and Acrylic Acid

Synthesis and Kinetics of Polyurethane-Acrylate Oligomer

Thermoresponsive behaviors of novel polyoxyethylene-functionalized acrylamide copolymers: Water solubility, rheological properties and surface activity

Preparation and Properties of Multi-Responsive Liquid Crystalline Poly(urethane-acrylate)s and Its Composite Membranes

Thermosensitive Poly(N-isopropylacrylamide-co-acrylonitrile) Hydrogels with Rapid Response

Thermoresponsive Property of Poly(N,N-bis(2-ethoxyethyl)acrylamide) and Its Multiblock Copolymers with Poly(N,N-dimethylacrylamide) Prepared by Hydrosilylation-Promoted Group Transfer Polymerization

UCST or LCST? Composition-Dependent Thermoresponsive Behavior of Poly(N-acryloylglycinamide-co-diacetone acrylamide)

Synthesis of thermo-responsive polymer gels composed of star-shaped block copolymers by copper-catalyzed living radical polymerization and click reaction

Biocompatible Thermoresponsive Polymers with Pendent Oligo(Ethylene Glycol) Chains and Cyclic Ortho Ester Groups

Acid‐labile, Thermoresponsive (meth)acrylamide Polymers with Pendant Cyclic Acetal Moieties

Water Soluble Hyperbranched Polymers from Controlled Radical Homopolymerization of Peg Diacrylate

2,5‐Dimethylfuran/Acrylonitrile as Latent Monomer for Sequence‐Controlled Copolymer and Sequence‐Dependent Thermo‐Responsivity

A Novel Polyurethane-Modified Poly(N-Isopropylacrylamide) Hydrogels

Thermal and Ph Responsive High Molecular Weight Poly(Urethane-Amine) with High Urethane Content

Tunable UCST thermoresponsive copolymers based on natural glycyrrhetinic acid

Aqueous Solution Properties of the Acid-Labile Thermoresponsive Poly(Meth)Acrylamides with Pendent Cyclic Orthoester Groups

Novel Acid‐Labile, Thermoresponsive Poly(methacrylamide)s with Pendent Ortho Ester Moieties