Rational Synthesis of Polymeric Nitrogen N 8 – with Ultraviolet Irradiation and Its Oxygen Reduction Reaction Mechanism Study with In Situ Shell-Isolated Nanoparticle-Enhanced Raman Spectroscopy

Zhenhua Yao,Zhiyi Wu,Maocong Hu,Safa Alzaim,Joshua Young,Jinchao Dong,Jinfa Chang,Haizheng Zhuang,El Mostafa Benchafia,Yang Yang,Jianfeng Li,Zafar Iqbal,Xianqin Wang

DOI: https://doi.org/10.1021/acscatal.1c03102

IF: 12.9

2021-10-13

ACS Catalysis

Abstract:Polynitrogen (PN) deposited on multiwalled carbon nanotubes was synthesized by cyclic voltammetry with ultraviolet (UV) irradiation. Compared to the sample formed without UV, a larger amount of N8– was synthesized and was found to distribute more uniformly on the MWNTs with 254 nm UV irradiation, indicating that the production of more azide (N3)0 radicals as the precursors for synthesis of N8– by photoexcitation of azide (N3–) ions is a rate-limiting step for PN synthesis. An oxygen reduction reaction kinetics study indicated a four-electron reaction pathway on N8–, whereas a two-electron process occurs on N3–. Analysis by in situ shell-isolated nanoparticle-enhanced Raman spectroscopy revealed that the side-on and end-on O2 adsorption occurred at N8– and N3–, respectively, confirming the electron transfer process. A full direct-methanol fuel cell study shows that methanol crossover typically reduces the current density of Pt/C by ∼40% but has very little effect on the performance of the PN-MWNT catalyst after testing for 120 h. Moreover, the power density from the PN-MWNT cathode is at least twice that from a Pt/C cathode.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acscatal.1c03102.The experimental details of material synthesis, characterizations, electrochemical measurement, DMFC test, and DFT calculations, UV–visible absorption spectrum of the azide anion determined by TDDFT (Figure S1), CV curves of 12 cycles for different samples (Figures S2–S4), temperature profiles of the electrolyte during CV synthesis (Figures S5 and S6), LSV curves (Figure S7), Koutecky–Levich plots (Figure S8), NBO partial charge distribution on an N8– anion (Figure S9), and calculated vibrational frequencies and Raman activity for O2 split and *OOH adsorption (Tables S1 and S2) (PDF)This article has not yet been cited by other publications.

chemistry, physical