UV‐curable 3D‐printable microwave‐absorbing material with a sword‐sheath structure based on multiwalled carbon nanotube/polypyrrole nanotube/Fe3O4 composites

Chuangji Liu,Yingjie Xu,Beiqing Huang,Wan Zhang,Xingyu Zhao,Yuxin Wang

DOI: https://doi.org/10.1002/adem.202400059

IF: 3.6

2024-05-07

Advanced Engineering Materials

Abstract:Multiwalled carbon nanotube (MWCNT)/polypyrrole nanotube (PPyNT)/Fe3O4 composites with a sword‐sheath structure are added to a UV‐curable resin to form a unique highly microwave‐absorbing material with a low absorbent content. Specifically tailored for high‐precision stereolithography three‐dimensional (3D) printers, the low absorbent content ensures an efficient curing and molding of the photosensitive resin. The conducting polymer polypyrrole is coated on the MWCNTs via free‐radical polymerization, forming a sheath structure. The initiator of the free‐radical polymerization, FeCl3, is converted into Fe3O4 and loaded onto the sheath structure. This ternary composite material is uniformly dispersed in the photosensitive resin with interconnected sword‐sheath structures, ensuring a favorable dielectric loss performance even at a low absorbent content. Importantly, the material exhibits both dielectric loss and magnetic loss properties. Using a UV‐cured microwave‐absorbing material with an absorbent content of 0.5 wt%, an electromagnetic loss of −22.5 dB can be achieved with a thickness of 1 mm. This UV‐cured microwave‐absorbing material facilitates the high‐precision 3D printing of microwave structures with various intricate shapes, broadening the application scope of microwave‐absorbing materials. This article is protected by copyright. All rights reserved.

materials science, multidisciplinary