Abstract:CsPbBr3 perovskite nanowires (NWs) with various lengths and widths have attracted much attention because of their attractive optoelectronic properties in optoelectronic devices. This study provides an effective approach to get size-controllable CsPbBr3 perovskite NWs based on the hot injection method. Oleylamine was used as the solvent to control the reaction speed, and CsPbBr3 perovskite NWs with adjustable widths and lengths were obtained by controlling the reaction time at 180 degrees C. X-ray diffraction, transmission electron microscopy (TEM), high-resolution transmission electronic microscopy, optical absorption, and photoluminescence (PL) spectra were carried out to investigate the structural evolution and growth mechanism. The results show that Cs4PbBr6 nanocrystals precipitated within 10 min and their amount reduced, and alpha-CsPbBr3 nanocrystals appeared and grew with the reaction time extending to 30 min. Cs4PbBr6 nanocrystals disappeared, and alpha-CsPbBr3 NWs with a width of similar to 20 nm and a length of similar to 1 mu m were obtained when the reaction reached 60 min. Further extending the reaction time resulted in self-assembling and growth of CsPbBr3 NWs, the width of CsPbBr3 wires reached similar to 1 mu m, and the length reached similar to 100 mu m when the reaction time was 24 h. TEM images clearly showed that CsPbBr 3 NWs become wider and longer by self-assembly of CsPbBr3 nanocubes and NWs. A statistics study revealed that there is a linear relationship between the width and the reciprocal of time. The self-assembly CsPbBr3 perovskite NWs presented a high-intensity green PL around 519 nm and high PL quantum yield, which was 71.7, 76.9, 64.9, and 39.5% for the samples reacted for 10, 30, 60, and 180 min, respectively, under 375 nm laser irradiation, and the photocarrier lifetime for the sample with 180 min can reach 25.79 ns. The obtained CsPbBr3 NWs have few defects and produce less recombination during the photoemission process, which is promising for applications in the fields of optoelectronic devices, especially photodetectors, lasers, and solar cells devices.

Amplifying Surface Energy Difference toward Anisotropic Growth of All‐Inorganic Perovskite Single‐Crystal Wires for Highly Sensitive Photodetector

Surface Energy‐Mediated Self‐Catalyzed CsPbBr3 Nanowires for Phototransistors

Inverse Growth of Large-Grain-Size and Stable Inorganic Perovskite Micronanowire Photodetectors.

All‐inorganic Perovskite Single‐Crystal Photoelectric Anisotropy

Synthesis of Size-Controllable Self-Assembled CsPbBr3 Perovskite Nanowires: Implications for Photoemission with Less Recombination

Solvothermal synthesis of cesium lead halide perovskite nanowires with ultra-high aspect ratios for high-performance photodetectors.

A-Site Cation Effect on Growth Thermodynamics and Photoconductive Properties in Ultrapure Lead Iodine Perovskite Monocrystalline Wires

High-performance Perovskite Photodetectors Based on CsPbBr3 Microwire Arrays.

2D Derivative Phase Induced Growth of 3D All Inorganic Perovskite Micro–Nanowire Array Based Photodetectors

Dipole-templated homogeneous grain growth of CsPbIBr2 films for efficient self-powered, all-inorganic photodetectors

Bidentate Ligand-Induced Oriented Transformation of CsPbBr3 Perovskite Nanocrystals into Nanowires for X-ray Photodetectors

Monolithically grown CSPbBr 3 by chemical vapor deposition for Self-Powered photodetector

Layered‐Perovskite Nanowires with Long‐Range Orientational Order for Ultrasensitive Photodetectors

On-Wire Design of Axial Periodic Halide Perovskite Superlattices for High-Performance Photodetection

Selective Surface Engineering of Perovskite Microwire Arrays

In-situ growth all-inorganic bismuth-based perovskite single crystal hexagonal sheets for planar photodetector

Surface ligand engineering of CsPbBr3 perovskite nanowires for high-performance photodetectors

Nucleation-Controlled Growth of High-Quality CsPbBr3 Single Crystal for Ultrasensitive Weak-Light Photodetector

A general method for growth of perovskite single-crystal arrays for high performance photodetectors

Nanochannel-confined Growth of Crystallographically Orientated Perovskite Nanowire Arrays for Polarization-Sensitive Photodetector Application

Epitaxial Growth of CsPbBr3 Pyramids/CdS Nanobelt Heterostructures for High-Performance Photodetectors