Constructing Densely Compacted Graphite/Si/SiO 2 Ternary Composite Anodes for High-Performance Li-Ion Batteries
Hao Wu,Lihua Zheng,Ning Du,Bowen Sun,Jie Ma,Yingying Jiang,Jiadong Gong,Huan Chen,Lianbang Wang
DOI: https://doi.org/10.1021/acsami.1c01877
2021-05-06
Abstract:Graphite has dominated the market of anode materials for lithium-ion batteries in applications such as consumer electronic devices and electric vehicles. As commercial graphite anodes are approaching their theoretical capacity, significant efforts have been dedicated towards higher capacity by blending capacity-enhancing additives (e.g., Si) with graphite particles. In spite of the improved gravimetric capacity, the areal capacity of such composite anodes might decrease due to excess void spaces and an incompatible material size distribution. Herein, a rational design of compact graphite/Si/SiO<sub>2</sub> ternary composites has been proposed to address the abovementioned issues. Si/SiO<sub>2</sub> clusters with an optimal particle size are homogeneously dispersed in the interstitial spaces between graphite particles to promote the packing density, leading to a higher areal capacity than that of pure graphite with equivalent mass loading or electrode thickness. By taking the full intrinsic advantages of graphite, Si, and SiO<sub>2</sub>, the composite electrodes exhibit 553.6 mAh g<sup>–1</sup> after 700 cycles with a capacity retention of 95.2%. Furthermore, the graphite/Si/SiO<sub>2</sub> electrodes demonstrate a high coulombic efficiency with an average of 99.68% from 2nd to 200th cycles and areal capacities above 1.75 mAh cm<sup>–2</sup> during 200 cycles with an areal mass loading as high as 4.04 mg cm<sup>–2</sup>. A packing model has been proposed and verified by experimental investigation as a design principle of densely compacted anodes. The effective strategy of introducing Si/SiO<sub>2</sub> clusters into the void spaces between graphite particles provides an alternative solution for implementation of graphite–Si composite anodes in next-generation Li-ion cells.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c01877?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c01877</a>.XRD patterns, SEM images, EDX mappings, XPS spectra, cycling performance, CV curves, voltage profiles, stabilized CEs, PSD curves, Nyquist plots, and detailed calculation of the lithium ion diffusion coefficient (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c01877/suppl_file/am1c01877_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology