Abstract:<p class="a-plus-plus">The high-temperature interactions between vanadium-titanium magnetite carbon composite hot briquettes (VTM-CCBs) and pellets were systematically investigated under simulated blast furnace conditions with respect to the reduction behavior, softening–melting–dripping characteristics, gas permeability, and Ti(C, N) precipitation mechanisms. The results showed that VTM-CCB charging can promote the reduction of the pellet in the packed bed and decrease the compressive strength of the pellet after reduction. The compressive strength of the VTM-CCB after reduction decreased with increasing temperature when the FC/O ratio (the ratio of the fixed carbon mol(C) in coal to the reducible oxygen mol(O) in iron oxides) was higher than 1.0. With an FC/O ratio lower than 1.0, the compressive strength of the VTM-CCB initially decreased and then increased. The FC/O ratio has a significant influence on the softening–melting interaction mechanism between the VTM-CCB and the pellet. With an FC/O ratio of 0.8, the bonding layer at the interface between the pellet and the VTM-CCB (consisting of molten fayalitic slag) can promote the softening process, thereby decreasing the softening start and end temperatures. By increasing the FC/O ratio to 1.4, a dense metallic iron shell with relatively high strength formed at the interface and restricted the collapse of the packed bed, thereby increasing the softening start and end temperatures and ensuring the transport of the reduction gas through the packed bed. The melting point of the primary slag phase increased with increasing FC/O ratio due to a decrease in the FeO content, which resulted in an increase in the melting start temperature from 1273 °C to 1294 °C (1546 K to 1567 K). The gas permeability in the cohesive zone increased with an increasing FC/O ratio of the VTM-CCB due to a combination of the skeletal role performed by the residual VTM-CCB and the decrease in the liquid slag proportion. In addition, as the FC/O ratio increased to 1.4, unconsumed carbon promoted the precipitation of Ti(C, N) at the slag–carbon and slag–metal interfaces, which resulted in a substantial increase in the dripping temperature and deterioration of the dripping behavior of the packed bed. Therefore, to suppress the precipitation of Ti(C, N) and improve the dripping behavior of the packed bed, the FC/O ratio of the charged VTM-CCB should be controlled within an appropriate range.</p>

Effect of nickel oxide additive on smelting mechanism of chromium-bearing vanadium titanomagnetite pellets

Effect of TiO2 on the Crushing Strength and Smelting Mechanism of High-Chromium Vanadium-Titanium Magnetite Pellets

Effect of diboron trioxide on the crushing strength and smelting mechanism of high-chromium vanadium–titanium magnetite pellets

Study on the High-temperature Properties of High-titania Slags produced with Cr-bearing Vanadia-titania Magnetite Smelting in Blast Furnace

Effect of V2O5 addition on the oxidation induration process of Hongge vanadium titanomagnetite pellet

Effect of MgO Addition on the Metallurgical Properties of the Vanadium-Titanium Pellet with Simulating Blast Furnace Conditions

Revealing the Softening-Melting Behaviors and Slag Characteristics of Vanadium-Titanium Magnetite Burden with Various MgO Addition

Effects of MnO on the smelting process of vanadium titanomagnetite pre-reduced pellets in an electric furnace

Effect of B2O3 on the Melting Characteristics and Slag-Matte Separation of Nickel Flash Furnace Melting

Pre-reduction of carbon-containing pellets of high chromium vanadium–titanium magnetite at different temperatures

High-Temperature Interactions Between Vanadium-Titanium Magnetite Carbon Composite Hot Briquettes and Pellets Under Simulated Blast Furnace Conditions

Effect of chromium content on the phase composition, crystallization and components extraction of vanadium slag

Softening–Melting Properties and Slag Evolution of Vanadium Titano-Magnetite Sinter in Hydrogen-Rich Gases

Effect and Function Mechanism of Sinter Basicity on Softening-Melting Behaviors of Mixed Burden Made from Chromium-Bearing Vanadium-Titanium Magnetite

Investigation of Basicity on Compressive Strength and Oxidation Induration Mechanism of Vanadium–Titanium Magnetite Pellets

The effect of nickel on the carbide precipitation behavior in Cr–Mo–V hot-working die steel

Effect of manganese ore and basicity on the consolidation characteristic of nickel‐chromium iron ore pellets

Study of the High Temperature Metallurgical Properties of On-Site Samples with Vanadium–Titanium Magnetite

Effect of MgO content in sinter on the softening–melting behavior of mixed burden made from chromium-bearing vanadium–titanium magnetite

Effect of Cr2O3 content on viscosity and phase structure of chromium-containing high-titanium blast furnace slag

Phase transformation and slag evolution of vanadium–titanium magnetite pellets during softening–melting process