Strong, tough, and elastic poly (vinyl alcohol)/polyacrylamide DN hydrogel based on Hofmeister effect for articular cartilage replacement
Cheng Yin,Zhiwu Huang,Yunge Zhang,Kaijing Ren,Songtao Liu,Honglin Luo,Quanchao Zhang,Yizao Wan
DOI: https://doi.org/10.1039/d3tb02637j
IF: 7.571
2024-02-21
Journal of Materials Chemistry B
Abstract:Traditional hydrogels are usually weak and brittle, which limit their application as articular cartilage replacement because the nature cartilage is generally strong, tough, and elastic. Therefore, it is highly desired to construct the hydrogels to mimic the mechanical properties of native articular cartilage. Herein, in this work, poly (vinyl alcohol)/polyacrylamide (PVA/PAM) DN hydrogels were prepared by in situ polymerization, which was then treated by Hofmeister series (Cit3-, SO42-, and Cl-) to achieve the H-PVA/PAM DN hydrogels. Among the three Hofmeister series, the DN hydrogel treated by Cit3- (named PVA/PAM-Cit) showed the densest microstructure and the highest crystallinity degree. In this context, PVA/PAM-Cit exhibited the tensile strength of 18.9 ± 1.6 MPa, compressive strength of 102.3 ± 7.9 MPa, tensile modulus of 10.6 ± 2.1 MPa, compressive modulus of 8.9 ± 0.8 MPa, and roughness of 66.2 ± 4.2 MJ m-3, respectively, which were the highest strength, modulus, and the second highest toughness when compared with the reported PVA and PVA based DN hydrogels so far. It also showed an extreme high elasticity, which could maintain the stress of 99.2% after 500 cycles fatigue test. Additionally, PVA/PAM-Cit can promote the adhesion, spreading and proliferation of chondrocytes. The results established that such strong, tough, and elastic hydrogel could be a novel candidate material for articular cartilage replacement.
materials science, biomaterials