Abstract:Plant fiber-reinforced polylactic acid (PLA) exhibits excellent mechanical properties and environmental friendliness and, therefore, has a wide range of applications. This study investigated the mechanical properties of three short plant fiber-reinforced PLA composites (flax, jute, and ramie) using mechanical testing and material characterization techniques (SEM, FTIR, and DSC). Additionally, we propose a methodology for predicting the mechanical properties of high-content short plant fiber-reinforced composite materials. Results indicate that flax fibers provide the optimal reinforcement effect due to differences in fiber composition and microstructure. Surface pretreatment of the fibers using alkali and silane coupling agents increases the fiber–matrix interface contact area, improves interface performance, and effectively enhances the mechanical properties of the composite. The mechanical properties of the composites increase with increasing fiber content, reaching the highest value at 40%, which is 38.79% higher than pure PLA. However, further increases in content lead to fiber agglomeration and decreased composite properties. When the content is relatively low (10%), the mechanical properties are degraded because of internal defects in the material, which is 40.42% lower than pure PLA. Through Micro-CT technology, the fiber was reconstructed, and it was found that the fiber was distributed mainly along the direction of injection molding, and the twin-screw process changes the shape and length of the fiber. By introducing the fiber agglomeration factor function and correcting the Halpin-Tsai criterion, the mechanical properties of composite materials with different contents were successfully predicted. Considering the complex stress state of composite materials in actual service processes, a numerical simulation method was established based on transversely isotropic material using the finite element method combined with theoretical analysis. The mechanical properties of high-content short plant fiber-reinforced composite materials were successfully predicted, and the simulation results showed strong agreement with the experimental results.

Relation between water absorption and mechanical properties of flax 3D braided yarn woven fabric PLA bio-degradable composites

Fabrication and mechanical properties of braided flax fabric polylactic acid bio-composites

Polylactide Composites Reinforced with Pre-Impregnated Natural Fibre and Continuous Cellulose Yarns for 3D Printing Applications

Moisture effect on tensile and low‐velocity impact tests of flax fabric‐reinforced PLA biocomposite

Thermo-Mechanical Properties of PLA/Short Flax Fiber Biocomposites

Effects of Wet and Dry Treatments on Surface Functional Groups and Mechanical Properties of Flax Fiber Composites

Pultrusion of flax/poly(lactic acid) commingled yarns and nonwoven fabrics

Mechanical Properties of PLA Specimens Obtained by Additive Manufacturing Process Reinforced with Flax Fibers

Experimental Investigation of Bi-Directional Flax with Ramie Fibre-Reinforced Phenol-Formaldehyde Hybrid Composites

Morphological modification of the technical flax fibre bundles to improve the longitudinal tensile properties of flax fibre reinforced epoxy composites

Enhancement of Thermal Behaviour of Flax with a Ramie Fibre-Reinforced Polymer Composite

Design and fabrication of high-performance 3D printed continuous flax fibre/PLA composites

PLA Composites Reinforced with Flax and Jute Fibers—A Review of Recent Trends, Processing Parameters and Mechanical Properties

Effect of Printing Parameters on Mechanical Behaviour of PLA-Flax Printed Structures by Fused Deposition Modelling

Mechanical Performances Analysis and Prediction of Short Plant Fiber-Reinforced PLA Composites

Analysis of Thermomechanical Behavior of the Tubular Braided Fabrics with Flax/Polyamide Commingled Yarns

Performance of Hybrid Composites Fabricated by Flax/Hemp Fibers Using Wire Mesh Plain Weaving Techniques

Thermomechanical Behavior of Methylene Diphenyl Diisocyanate-Bonded Flax/Glass Woven Fabric Reinforced Laminated Composites

Examining the performance of eco-friendly flax fiber composites: mechanical, thermal and durability properties—review

Experimental Investigation on Volume Fraction of Mechanical and Physical Properties of Flax and Bamboo Fibers Reinforced Hybrid Epoxy Composites

Investigations on the mechanical properties of PLA/Flax fibre composites obtained by Fused Filament Fabrication