Abstract:Doped ceria-based metal oxides are widely used as supports and stand-alone catalysts in reactions where CO2 is involved. Thus, it is important to understand how to tailor their CO2 adsorption behavior. In this work, steering the CO2 activation behavior of Ce-La-Cu-O ternary oxide surfaces through the combined effect of chemical and mechanical strain was thoroughly examined using both experimental and ab initio modeling approaches. Doping with aliovalent metal cations (La3+ or La3+/Cu2+) and post-synthetic ball milling were considered as the origin of the chemical and mechanical strain of CeO2, respectively. Experimentally, microwave-assisted reflux-prepared Ce-La-Cu-O ternary oxides were imposed into mechanical forces to tune the structure, redox ability, defects, and CO2 surface adsorption properties; the latter were used as key descriptors. The purpose was to decouple the combined effect of the chemical strain (εC) and mechanical strain (εM) on the modification of the Ce-La-Cu-O surface reactivity toward CO2 activation. During the ab initio calculations, the stability (energy of formation, EOvf) of different configurations of oxygen vacant sites (Ov) was assessed under biaxial tensile strain (ε > 0) and compressive strain (ε < 0), whereas the CO2-philicity of the surface was assessed at different levels of the imposed mechanical strain. The EOvf values were found to decrease with increasing tensile strain. The Ce-La-Cu-O(111) surface exhibited the lowest EOvf values for the single subsurface sites, implying that Ov may occur spontaneously upon Cu addition. The mobility of the surface and bulk oxygen anions in the lattice contributing to the Ov population was measured using 16O/18O transient isothermal isotopic exchange experiments; the maximum in the dynamic rate of 16O18O formation, Rmax(16O18O), was 13.1 and 8.5 μmol g-1 s-1 for pristine (chemically strained) and dry ball-milled (chemically and mechanically strained) oxides, respectively. The CO2 activation pathway (redox vs associative) was experimentally probed using in situ diffuse reflectance infrared Fourier transform spectroscopy. It was demonstrated that the mechanical strain increased up to 6 times the CO2 adsorption sites, though reducing their thermal stability. This result supports the mechanical actuation of the "carbonate"-bound species; the latter was in agreement with the density functional theory (DFT)-calculated C-O bond lengths and O-C-O angles. Ab initio studies shed light on the CO2 adsorption energy (Eads), suggesting a covalent bonding which is enhanced in the presence of doping and under tensile strain. Bader charge analysis probed the adsorbate/surface charge distribution and illustrated that CO2 interacts with the dual sites (acidic and basic ones) on the surface, leading to the formation of bidentate carbonate species. Density of states (DOS) studies revealed a significant Eg drop in the presence of double Ov and compressive strain, a finding with design implications in covalent type of interactions. To bridge this study with industrially important catalytic applications, Ni-supported catalysts were prepared using pristine and ball-milled oxides and evaluated for the dry reforming of methane reaction. Ball milling was found to induce modification of the metal-support interface and Ni catalyst reducibility, thus leading to an increase in the CH4 and CO2 conversions. This study opens new possibilities to manipulate the CO2 activation for a portfolio of heterogeneous reactions.

Activation of carbon dioxide on zinc oxide surfaces doped with cerium

A comparative DFT+U study of CO oxidation on Pd- and Zr-doped ceria

The pivotal role of oxygen vacancy and surface hydroxyl in the adsorption and activation of CO 2 on ceria-zirconia mixed oxide

Direct Co Oxidation by Lattice Oxygen on Zr-Doped Ceria Surfaces

Lattice Oxygen Activation in Transition Metal Doped Ceria

Carbon dioxide adsorption and activation on Ceria (110): A density functional theory study

Oxygen vacancy formation and their role in the CO2 activation on Ca doped ZrO2 surface: An ab-initio DFT study

Decoupling the Chemical and Mechanical Strain Effect on Steering the CO2 Activation over CeO2-Based Oxides: An Experimental and DFT Approach

Oxygen vacancy enhancing CO2 electrochemical reduction to CO on Ce-doped ZnO catalysts

Transition-Metal-Doped CeO2 for the Reverse Water-Gas Shift Reaction: An Experimental and Theoretical Study on CO2 Adsorption and Surface Vacancy Effects

Enhanced oxygen vacancy formation in ceria (111) and (110) surfaces doped with divalent cations

Activating Surface Lattice Oxygen of a Cu/Zn 1 –x Cu x O Catalyst through Interface Interactions for CO Oxidation

Enhanced photocatalytic activity of Ce-doped ZnO nanopowders synthesized by combustion method

Design Aspects of Doped CeO2 for Low-Temperature Catalytic CO Oxidation: Transient Kinetics and DFT Approach

Activating Surface Lattice Oxygen of a Cu/Zn<sub>1-<i>x</i></sub>Cu<i><sub>x</sub></i>O Catalyst through Interface Interactions for CO Oxidation

Morphology-dependent Photoelectric Properties and Photocatalytic CO2 Reduction of Zinc Porphyrin Nanocrystals

A Theoretic Insight Into The Catalytic Activity Promotion Of Ceo2 Surfaces By Mn Doping

Synergistic Effects of Cu2O-decorated CeO2 on Photocatalytic CO2 Reduction: Surface Lewis Acid/base and Oxygen Defect

Oxygen Vacancy Generation and Stabilization in CeO2–x by Cu Introduction with Improved CO2 Photocatalytic Reduction Activity

Co2 Photoreduction with H2o Vapor on Highly Dispersed Ceo2/Tio2 Catalysts: Surface Species and Their Reactivity