Effects of oxygen vacancy defect on microwave pyrolysis of biomass to produce high-quality syngas and bio-oil: Microwave absorption and in-situ catalytic

Junhao Lin,Shichang Sun,Juan Luo,Chongwei Cui,Rui Ma,Lin Fang,Xiangli Liu

DOI: https://doi.org/10.1016/j.wasman.2021.05.002

IF: 8.816

2021-06-01

Waste Management

Abstract:<p>This paper proposed to use ferric oxide (Fe₂O₃) and ferroferric oxide (Fe₃O₄) as catalysts with both microwave absorption and catalytic properties. Carbon dioxide (CO₂) was introduced as the reaction atmosphere to further improve the quality of biofuel produced by microwave pyrolysis of food waste (FW). The results showed the bio-gas yield and the syngas concentration (H₂ + CO) increased to 70.34 wt% and 61.50 mol%, respectively, using Fe₃O₄ as the catalyst. The content of aliphatic hydrocarbons in bio-oil produced with the catalyst Fe₂O₃ increased to 67.48% and the heating value reached 30.45 MJ/kg. Compared with Fe₂O₃ catalyst, Fe₃O₄ exhibited better microwave absorption properties and catalytic properties. Transmission electron microscopy (TEM) and Electron paramagnetic resonance (EPR) characterizations confirmed that the crystal surface of Fe₃O₄ formed more oxygen vacancy defects and unpaired electrons. Additionally, according to the X-ray photoelectron spectroscopy (XPS) analysis, the content of lattice oxygen in Fe₃O₄ was 14.11%, a value that was much lower than Fe₂O₃ (38.54%). The oxygen vacancy defects not only improved the efficient utilization of microwave energy but also provided the reactive sites for the reaction between the volatile organic compounds (VOCs) and CO₂ to generate CO. This paper provides a new perspective for selecting catalysts that have both microwave absorption and catalytic properties during the microwave pyrolysis of biomass.</p>

environmental sciences,engineering, environmental

What problem does this paper attempt to address?

The paper primarily explores the impact and mechanism of oxygen vacancy defects in the process of microwave pyrolysis of biomass to produce high-quality syngas and bio-oil. The study used iron oxide (Fe₂O₃) and magnetite (Fe₃O₄) as catalysts and conducted experiments in a carbon dioxide atmosphere.

### Research Objectives

1. **Improve Biomass Microwave Pyrolysis Efficiency**: By adding catalysts (Fe₂O₃ and Fe₃O₄) with microwave absorption properties, the aim is to enhance the energy conversion efficiency of biomass (such as food waste) during the microwave pyrolysis process.

2. **Enhance Biofuel Quality**: Investigate the effects of different catalysts on the yield and composition of biogas and the quality of bio-oil during microwave pyrolysis in a carbon dioxide atmosphere.

3. **Explore the Role of Oxygen Vacancy Defects**: Analyze how oxygen vacancy defects affect the microwave absorption and catalytic performance of the catalysts, and how these defects promote the reaction between volatile organic compounds and carbon dioxide to produce carbon monoxide.

### Main Findings

- When using Fe₃O₄ as a catalyst, the biogas yield reached 70.34%, and the concentration of syngas (hydrogen + carbon monoxide) reached 61.50 mol%.
- The bio-oil produced under Fe₂O₃ catalysis had an increased alkane content of 67.48% and a heating value of 30.45 MJ/kg.
- Fe₃O₄ exhibited better microwave absorption and catalytic performance compared to Fe₂O₃, which is related to the formation of more oxygen vacancy defects and unpaired electrons on the surface of Fe₃O₄.
- The lattice oxygen content of Fe₃O₄ is lower than that of Fe₂O₃. Oxygen vacancy defects not only improve the effective utilization of microwave energy but also provide active sites necessary for the reaction between volatile organic compounds and carbon dioxide to produce carbon monoxide.

In summary, this study provides a new perspective for selecting catalysts with dual functions of microwave absorption and catalysis, which helps to improve the efficiency and product quality of biomass microwave pyrolysis.