Fe2O3 nanowire arrays on Ni-coated yarns as excellent electrodes for high performance wearable yarn-supercapacitor
Xuhao Wu,Yuhua Chen,Kaijie Liang,Xueang Yu,Qinqin Zhuang,Qiao Yang,Shaofeng Liu,Shuang Liao,Na Li,Haiyan Zhang
DOI: https://doi.org/10.1016/j.jallcom.2020.158156
IF: 6.2
2021-06-01
Journal of Alloys and Compounds
Abstract:<p>Fibrous supercapacitors with high energy/power densities are important energy supply systems for smart wearable devices. Kinds of yarn-cathodes were fabricated, however, high performance anode materials have not been developed to match with the reported cathodes. Additionally, the (volumetric/area) capacitance of yarn-supercapacitors are often limited by less active material deposition, as the yarn is not resistant to high temperature, and the metal conductive-layer is not corrosion resistant. So, a high mass-loading anode with high volumetric performance has not been fabricated. In this study, we report a novel kind of Fe<sub>2</sub>O<sub>3</sub> nanowires arrays on Ni-coated textiles anodes to solve this problem. The nickel layer deposited on the low-cost polyester yarn was applied as high-conductivity current collector, and vertically aligned Fe<sub>2</sub>O<sub>3</sub> nanowires grown on the nickel layer with high mass loading were used as high performance active materials (Fe<sub>2</sub>O<sub>3</sub>//Ni//Yarn). It's worth noting that the Fe<sub>2</sub>O<sub>3</sub>//Ni//Yarn-based anodes exhibit a high specific capacitance of 54.2 F cm<sup>-3</sup> at a scan rate of 10 mv s<sup>-1</sup>, furthermore, a symmetrical all-solid-state yarn-supercapacitor based on the above electrodes show a capacitance of 969 mF cm<sup>-3</sup> at 10 mv s<sup>-1</sup>. This work provide a good choice of yarn-anodes to match with the reported high performance cathodes for further yarn-supercapacitor designs.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering