Unraveling radiation damage and healing mechanisms in halide perovskites using energy-tuned dual irradiation dosing

Ahmad R. Kirmani,Todd A. Byers,Zhenyi Ni,Kaitlyn VanSant,Darshpreet K. Saini,Rebecca Scheidt,Xiaopeng Zheng,Tatchen Buh Kum,Ian R. Sellers,Lyndsey McMillon-Brown,Jinsong Huang,Bibhudutta Rout,Joseph M. Luther

DOI: https://doi.org/10.1038/s41467-024-44876-1

IF: 16.6

2024-01-24

Nature Communications

Abstract:Abstract Perovskite photovoltaics have been shown to recover, or heal, after radiation damage. Here, we deconvolve the effects of radiation based on different energy loss mechanisms from incident protons which induce defects or can promote efficiency recovery. We design a dual dose experiment first exposing devices to low-energy protons efficient in creating atomic displacements. Devices are then irradiated with high-energy protons that interact differently. Correlated with modeling, high-energy protons (with increased ionizing energy loss component) effectively anneal the initial radiation damage, and recover the device efficiency, thus directly detailing the different interactions of irradiation. We relate these differences to the energy loss (ionization or non-ionization) using simulation. Dual dose experiments provide insight into understanding the radiation response of perovskite solar cells and highlight that radiation-matter interactions in soft lattice materials are distinct from conventional semiconductors. These results present electronic ionization as a unique handle to remedying defects and trap states in perovskites.

multidisciplinary sciences

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to understand the self - healing mechanism of halide perovskite solar cells (PSCs) after radiation damage. Specifically, through the design of a two - dose experiment, the researchers first irradiated the device with low - energy protons (0.06 MeV). These protons mainly cause non - ionizing energy loss (NIEL), resulting in atomic displacement; then irradiated with high - energy protons (1.0 MeV). These protons have a higher ionizing energy loss (IEL) and can effectively repair the initial radiation damage and restore the device efficiency. By combining simulation and experiment methods, the researchers discussed in detail the interaction between protons of different energies and perovskite materials, and how these interactions affect the performance of PSCs.

### Core problems of the paper
1. **Radiation damage mechanism**: How does the non - ionizing energy loss (NIEL) caused by low - energy protons (0.06 MeV) lead to atomic displacement and performance degradation in perovskite solar cells?
2. **Self - healing mechanism**: How does the ionizing energy loss (IEL) caused by high - energy protons (1.0 MeV) repair the damage caused by NIEL through local heating and lattice vibration, thereby restoring or improving the performance of PSCs?
3. **Differences in radiation response**: Why are the effects of different - energy protons on PSCs different from those of traditional semiconductor materials, especially in soft - lattice materials?

### Main findings
- **Influence of NIEL and IEL**: Low - energy protons mainly cause atomic displacement through NIEL, resulting in performance degradation; while high - energy protons can repair these damages and restore or even improve the performance of PSCs through local heating and lattice vibration caused by IEL.
- **Two - dose experiment**: Through the two - dose experiment, the researchers were able to independently adjust the ratio of NIEL and IEL, thereby more accurately exploring the influence of protons of different energies on PSCs.
- **Defect types and distribution**: Through thermal admittance spectroscopy (TAS) analysis, the researchers found the changes of different types of trap states after radiation, further verifying the self - healing mechanism.

### Experimental methods
- **Two - dose experiment**: First, irradiate PSCs with low - energy protons (0.06 MeV), and then perform secondary irradiation with high - energy protons (1.0 MeV).
- **Simulation calculation**: Use the SRIM (Stopping and Range of Ions in Matter) code to simulate the interaction between protons and PSCs and predict the distribution of NIEL and IEL.
- **Performance test**: Evaluate the performance changes of PSCs under different radiation conditions by measuring parameters such as current - voltage (J - V) curves and time - resolved photoluminescence lifetime (TRPL).

### Conclusion
This research provides important insights for understanding the radiation tolerance of perovskite solar cells in the space environment. In particular, through the two - dose experiment, it reveals the important role of ionizing energy loss (IEL) in repairing radiation damage. This not only helps to develop more radiation - resistant perovskite solar cells, but also provides a theoretical basis for further research on the radiation response of other soft - lattice materials.