Abstract:This study examines the effectiveness of W/O microemulsion mediated Sm2S3 nanospheres in Pickering emulsion based Crystal violet (CV) dye degradation and PANI@Sm2S3 nanocomposites synthesis. Evaluation of nanospheres inside the core of reverse micelles are detected through DLS, TEM and FESEM instrumentations. The formation of nanospheres involve two phases: nucleation phase (5-30 min) and growth phase (30-120 min). Through in situ hydrophobization of negatively charged (with zeta value -4.47 mV at neutral pH) Sm2S3 nanoparticles (0.1 wt.%) with a suitable amount of a cationic CTAB surfactant, a stable O/W Pickering emulsions have been developed. 0.1 wt.% Sm2S3 in situ hydrophobized with 2.7 mM CTAB offered a stable Pickering emulsion with a diameter of 23 m, after 1 day of storage. This Pickering emulsion improves local concentration of CV by efficiently encapsulating dye molecules inside the core of emulsion droplets. Therefore, dye molecules get numerous opportunity to interact with the photocatalyst, Sm2S3, and efficiently degrade. Pickering emulsion stabilised by 0.1 wt.% of Sm2S3 nanoparticles in situ hydrophobized with 2.7 mM of CTAB results almost 100% degradation. Moreover, by using only solid Sm2S3 (having wt.% of 0.025 or 0.075) as a Pickering stabiliser, new PANI@Sm2S3 spherical nanocomposites are synthesised via Pickering emulsion polymerization. The formation of PANI@Sm2S3 composites are identified by UV, IR, and 1H-NMR investigations. Analysis of FESEM images showed that the amount of wt.% nanoparticles used in dispersion (for 0.025 wt.%, 35 nm and 0.075 wt.%, 29 nm) strongly influences the size and shape of the composites.

A deeper insight into the evaluation of water-in-oil microemulsions templated samarium sulfide nanospheres: explored its role in Pickering emulsion formulation for photocatalytic dye degradation and synthesis of PANI@Sm2S3 nanocomposites