Abstract:Magnesium hydroxide, as a green inorganic flame-retardancy additive, has been widely used in polymer flame retardancy. However, magnesium hydroxide is difficult to disperse with epoxy resin (EP), and its flame-retardancy performance is poor, so it is difficult to use in flame-retardant epoxy resin. In this study, an efficient magnesium hydroxide-based flame retardant (MH@PPAC) was prepared by surface modification of 2-(diphenyl phosphine) benzoic acid (PPAC) using a simple method. The effect of MH@PPAC on the flame-retardancy properties for epoxy resins was investigated, and the flame-retardancy mechanism was studied. The results show that 5 wt% MH@PPAC can increase the limiting oxygen index for EP from 24.1% to 38.9%, achieving a V-0 rating. At the same time, compared to EP, the peak heat release rate, peak smoke production rate, total smoke production rate, and peak CO generation rate for EP/5 wt% MH@PPAC composite material decreased by 53%, 45%, 51.85%, and 53.13% respectively. The cooperative effect for PPAC and MH promotes the formation of a continuous and dense char layer during the combustion process for the EP-blend material, significantly reducing the exchange for heat and combustible gases, and effectively hindering the combustion process. Additionally, the surface modification of PPAC enhances the dispersion of MH in the EP matrix, endowing EP with superior mechanical properties that meet practical application requirements, thereby expanding the application scope for flame-retardant EP-blend materials.
What problem does this paper attempt to address?
The main problem that this paper attempts to solve is to improve the flame - retardant performance of epoxy resin (EP). Specifically, in view of the poor dispersibility and unsatisfactory flame - retardant effect of magnesium hydroxide (MH) in epoxy resin, the author proposed a surface - modification strategy by 2 - (diphenylphosphino) benzoic acid (PPAC) and prepared the highly efficient flame - retardant MH@PPAC. Through this method, it aims to improve the dispersibility of MH in epoxy resin, thereby significantly enhancing the flame - retardant and mechanical properties of the composite material.
### Main research contents:
1. **Background and problems**:
- Epoxy resin (EP), as a thermosetting polymer material, is widely used in construction, electronics, aerospace and other fields because of its excellent thermal stability, electrical insulation, chemical resistance and mechanical properties.
- However, EP is flammable and will produce a large amount of harmful gases and smoke when burning, which poses a threat to human life and property safety.
- Magnesium hydroxide (MH), as a green inorganic flame - retardant additive, although has a good smoke - suppression effect, its dispersibility in epoxy resin is poor, resulting in an unsatisfactory flame - retardant performance.
2. **Solutions**:
- A new type of flame - retardant MH@PPAC was prepared by surface - modifying MH with 2 - (diphenylphosphino) benzoic acid (PPAC).
- The influence of MH@PPAC on the flame - retardant performance of epoxy resin was studied, and its flame - retardant mechanism was explored.
3. **Experimental methods**:
- **Material preparation**: A series of epoxy resin composites containing MH or MH@PPAC were prepared by a simple mixing method.
- **Characterization methods**: Techniques such as FTIR, XPS, HRMS, TGA, DTG, SEM were used to characterize the structure, chemical composition, thermal stability and micro - morphology of the materials.
- **Performance tests**: The flame - retardant performance of the composites was evaluated by limiting oxygen index (LOI), vertical burning test (UL - 94) and cone calorimeter test (CCT).
4. **Results and discussions**:
- **Thermal stability**: The introduction of MH@PPAC significantly improved the thermal stability of epoxy resin and delayed the initial degradation temperature.
- **Mechanical properties**: Although the tensile strength of the composite decreased after adding MH@PPAC, it was still significantly better than that of unmodified MH and PPAC.
- **Flame - retardant performance**: The addition of 5 wt% MH@PPAC increased the LOI value of epoxy resin from 24.1% to 38.9%, reaching the UL - 94 V - 0 level. At the same time, the peak heat release rate (PHRR), peak smoke production rate (SPR), total smoke production rate (TSP) and peak CO production rate of the composite were respectively reduced by 53%, 45%, 51.85% and 53.13%.
- **Flame - retardant mechanism**: The synergistic effect of MH@PPAC promoted the formation of a continuous and dense char layer during the combustion process, significantly reducing the exchange of heat and combustible gases and effectively hindering the combustion process.
### Conclusion:
By surface - modifying magnesium hydroxide (MH) with 2 - (diphenylphosphino) benzoic acid (PPAC), the highly efficient flame - retardant MH@PPAC was successfully prepared. This flame - retardant not only significantly improves the flame - retardant performance of epoxy resin, but also improves its mechanical properties, making it have a broader prospect in practical applications.