Abstract:Steel rebars with oxide scale, which is usually rich of defects, are widely used in industry. On the surface of the oxide scale, it is difficult to prepare a conversion film with desirable corrosion resistance because of the acidity of conventional conversion solutions. In this work, a sol–gel solution (pH = 11) was employed to retard the diffusion of cerium ions avoiding the formation of cerium salt precipitates at room temperature. After treatments, the diffusion of cerium ions would be accelerated and a protective conversion film would form to repair natural defects on oxide scale of steel rebars at a higher temperature. This strategy can not only avoid the peeling of the oxide scale by the acid solution, but also prevent a large amount of non-uniform precipitation of the film-forming Ce3+ ions. The conversion film@oxide scale was characterized by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), electrochemical impedance spectroscopy (EIS), potentiodynamic polarization curve (PPC) etc. It is found that the corrosion resistance of the prepared film@oxide scale was enhanced greatly when the concentration of added cerium ion (III) was 0.5 M, with pH adjusted to 11. After 30 days of immersion, R ct of surface treated rebar is more 180 times that of blank sample. The excellent corrosion resistance is closely related to the double-layer structure of the prepared sol-gel film, especially an about 2 nm inner layer of cerium oxide.

Investigation of the inhibiting effect of environmentally friendly cerium-containing conversion films on the corrosion of zinc coatings

Corrosion Resistance Behavior of Zinc Substrate Treated with Rare Earth Salt Passivation

Changes of Corrosion Electrochemical Behavior of Cerium Nitrate Doped GPTMS/TEOS Silane Hybrid Films with Immersion Time

Electrochemical Behavior of Organic and Inorganic Zinc-Rich Coatings in 3.5% NaCl Solution

Corrosion-Resistive ZrO2 Barrier Films on Selected Zn-Based Alloys

Corrosion Characteristics of Chromated Zinc in Sodium Chloride Solutions

Effect of cerium salts on the cut-edge of zinc-based sacrificial coatings: Influence of Al and Mg alloying elements on galvanic corrosion

Semiconductor Property and Corrosion Behavior of Passive Film Formed on Steel with Zinc Coating in 5% NaCl Solution

Effect of Na2CO3 on Corrosion Resistance of Cerium Conversion Film on Mg–Gd–Y–Zr Magnesium Alloy Surface

Synthesis and Evaluation of Corrosion Resistance of Molybdate-Based Conversion Coatings on Electroplated Zinc

Effect of Citric Acid on Cerium Conversion Coating of Hot-Dip Galvanized Steel

THE INHIBITION EFFECT OF ZINC AND SILICATE IONS ON PITTING CORROSION INDUCED BY CERIUM(III) IONS OF CARBON STEEL IN SODIUM CHLORIDE SOLUTION

Influence of the Chemical Composition of Ceria Conversion Coatings, Sealed in Solution of NaH2PO4 and Ca(NO3)2, on the Corrosion Behavior of Aluminum

Corrosion Resistance of Cerium-Doped Zinc Calcium Phosphate Chemical Conversion Coatings on AZ31 Magnesium Alloy

The Effect of Surface Modification of Zinc Particles with Phosphoric Acid on the Corrosion Resistance of Cold Galvanizing Coatings

Growth behaviour of cerium‐based conversion coating on Zn‐5%Al alloy

In-situ chemical conversion film for stabilizing zinc metal anodes

Investigation Progress of Rare Earth Conversion Coating on Zinc and Zinc Coatings

On the Corrosion Resistance of Porous Electroplated Zinc Coatings in Different Corrosive Media

Stabilization of Zn Metal Anode through Surface Reconstruction of a Cerium‐Based Conversion Film

Construction of Ce3+ modified conversion film on oxide scale of plain steel rebars to greatly enhance the corrosion resistance