Modification in Surface Properties of Bismuth after Thermal Plasma Treatment
Muhammad Arif Mehmood,Shazia Bashir,Asma Hayat,Muhammad Shahid Rafique,Muhammad Hamza,Sajid Ali,Syed Muhammad Kamran Shabbir,Ammar Afzal
DOI: https://doi.org/10.1007/s11665-024-09214-y
IF: 2.3
2024-02-13
Journal of Materials Engineering and Performance
Abstract:The present study deals with the designing and fabrication of an experimental setup for argon (Ar) thermal plasma generation and its implementation for surface structuring along with modifications in morphological, compositional, electrical, contact angle and mechanical properties of Bismuth (Bi). Ar plasma parameters have been investigated by using a solid state nuclear track detector (SSNTD). In the present work, polycrystalline Bi has been treated at various Ar gas flow rates ranging from 10 to 25 L/min for a fixed time interval of 10 minutes. Bi targets were also treated at different treatment times ranging from 10 to 25 minutes at constant gas flow rate of 15 L/min. Optical microscopy and scanning electron microscope (SEM) analyses reveal the melting, evaporation, splashing, collisional sputtering, coalescence fusion and ejection of materials at different gas flow rates which are responsible for the formation of protrusions, cavities, cones, particulates, melt pools and agglomerates. At different treatment timings, ejection of materials, thermal desorption, reattachments, re-solidification and recrystallization are responsible for particulates, cavities and conical spike formation. XRD patterns reveal the slightly higher angular peak shifting and intensity enhancement at the lowest gas flow rate and treatment time. At the highest flow rate and treatment time, some new phases of Bi 2 O 3 are identified. However, an increasing trend in peak intensity, crystallite size, induced stresses and the decreasing trend in dislocation line density is observed with increasing the thermal plasma treatment time and flow rate which are attributed to improved crystalline nature. FTIR analysis shows a considerable increase in existing peak intensities of BiO without the identification of a new band in plasma-treated Bi. After thermal plasma treatment, the decreasing trends in electrical conductivity along with contact angle and increasing trends in hardness are attributed to enhancements in defect generation and surface roughness.
materials science, multidisciplinary